《噴涂速凝高分子液體橡膠防水膠膜應用技術規(guī)程》

ICS號中國標準文獻分類號中國城市科學研究會標準T/CSUSXX-202X噴涂速凝高分子液體橡膠防水膠膜應用技術規(guī)程Applicationtechnicalregulationsofsprayingquick-settingpolymerliquidrubberwaterproofingmembrane（征求意見稿）XXXX-XX-XX發(fā)布XXXX-XX-XX實施中國城市科學研究會發(fā)布目次1總則···························································································22術語·························································································33基本規(guī)定····················································································44材料···················································································55設計···················································································85.1一般規(guī)定················································································85.2屋面防水工程···································································85.3地下防水工程···································································125.4地鐵及隧道防水工程···································································156施工···················································································196.1一般規(guī)定···············································································196.2基層處理···································································196.3施工準備···································································206.4噴涂施工···································································206.5搭接和甩槎的操作方法································································216.6保護層施工···································································227工程驗收···················································································237.1一般規(guī)定···············································································237.2主控項目···································································247.3一般項目···································································258安全和環(huán)境保護············································································268.1成品保護···············································································268.2安全注意事項···································································26附錄A噴涂速凝高分子液體橡膠防水膠膜A組分現(xiàn)場檢驗方法···············27附錄B噴涂速凝高分子液體橡膠防水膠膜制備方法···············28本標準用詞說明····························································29引用標準名錄·····················································································301總則為規(guī)范噴涂速凝高分子液體橡膠防水膠膜的設計、施工及工程驗收，保證工程質量，實現(xiàn)高質量發(fā)展及滿足國家環(huán)保節(jié)能要求和規(guī)范施工做法，制定本標準。本標準適用于市政及建筑防水工程?？蓱糜诘罔F車站、隧道、污水處理廠、垃圾填埋場、公路、橋梁，還可應用于鐵路橋面、化工、水利、尾礦庫抗?jié)B、海港碼頭、管理設施及等防腐蝕、防滲漏工程。噴涂速凝高分子液體橡膠防水膠膜的設計、施工及驗收除應符合本標準外，尚應符合國家、行業(yè)和地方現(xiàn)行有關規(guī)范和標準的規(guī)定。

2術語噴涂速凝高分子液體橡膠防水膠膜技術系統(tǒng)technicalsystemofpremiumliquidrubber是由噴涂速凝高分子液體橡膠防水膠膜、專用噴涂設備和噴涂方法完成防水功能的系統(tǒng)。噴涂速凝高分子液體橡膠防水膠膜sprayingrapid-setsyntheticliquidrubberwaterproofingmembrane噴涂速凝高分子液體橡膠防水膠膜是由合成高分子聚合物和超細、懸浮、微乳型改性乳化瀝青為主要材料，以水為介質，并添加助劑，經(jīng)加工制成A、B組分，經(jīng)專用設備噴涂，快速固化為防水橡膠層。具有無污染、易操作、高彈性、耐老化的特點。噴涂速凝高分子液體橡膠防水膠膜A組分partAofsprayingrapid-setsyntheticliquidrubberwaterproofingmembraneA組分是由合成高分子聚合物和超細、懸浮、微乳型改性乳化瀝青構成的混合物。噴涂速凝高分子液體橡膠防水膠膜B組分partBofsprayingliquidrubberB組分是由一定濃度的輕金屬鹽構成的水溶液。專用噴涂設備specialsprayingequipment專用噴涂設備是由一個發(fā)動機帶動的雙泵、雙管、雙槍、雙路進、回流管組成的噴涂設備。噴涂方法sprayingmethod將A組分和B組分分別置于兩個不同的容器中，啟動專用噴涂設備的發(fā)動機，帶動兩個低壓高流量流體泵，扣動控制兩管噴槍的扳機，A組分和B組分同時噴出交合，瞬時反應，一次，數(shù)遍，橫豎交叉噴涂，不需要間歇，落在待噴涂的物體上形成有一定厚度的膠膜。噴涂速凝高分子液體橡膠防水膠膜適用基底applicablesubstrate噴涂速凝高分子液體橡膠防水膠膜適用的基底：是指由混凝土、金屬、木頭、磚瓦、石棉瓦、土、沙和石頭、塑料、玻璃、布及各種卷材與防水粘接的基礎。噴涂速凝高分子液體橡膠防水膠膜加強層reinforcementlayer采用無紡布、土工布或丙綸布，裁剪至合適的尺寸，使用噴涂速凝高分子液體橡膠防水膠膜A組份浸漬或空鋪，鋪貼在基層上用以提高局部膠膜的抗拉強度和改善其延伸率的措施構造。

3基本規(guī)定根據(jù)建筑物的性質、重要程度、防水設防等級、使用功能等，選擇適宜的噴涂膠膜厚度。噴涂速凝高分子液體橡膠防水膠膜為“皮膚式”防水技術系統(tǒng)，膠膜與基底不竄水、不剝離，設計可采用單層防水設計。本防水膠膜單層使用時其防水膠膜設計厚度不應小于2.4mm。本防水膠膜作為一道防水層時厚度為1.5mm。建筑與市政工程設計及工程防水做法應依據(jù)工程防水等級和工程類別確定，符合GB55030并應按3.0.2表選用。表3.0.2工程防水等級和工程類別單位為：mm防水等級工程類別屋面工程地下工程建筑外墻建筑室內道橋及蓄水工程地鐵隧道I級1.5+II級1.5-噴涂速凝高分子液體橡膠防水膠膜防水工程應根據(jù)工程的使用環(huán)境及膠膜的耐候性，選擇合適的保護措施。噴涂速凝高分子液體橡膠防水膠膜防水工程所采用的材料之間應具有相容性。

4材料噴涂速凝高分子液體橡膠防水膠膜、涂刷型橡膠瀝青防水涂料應進行進場檢驗，并符合下列規(guī)定：噴涂速凝高分子液體橡膠防水膠膜的性能要求和試驗方法應符合表4.0.1的規(guī)定。表4.0.1噴涂速凝高分子液體橡膠防水膠膜的性能指標和試驗方法序號項目指標試驗方法I型II型固體含量/％≥5555GB/T16777凝膠時間/s≤55GB/T23446平均粒徑/um≤33GB/T19077實干時間/h≤88GB/T16777耐熱度（120±2）℃（140±2）℃GB/T16777無流淌、滑動、滴落GB/T16777不透水性0.3MPa，120min不透水GB/T16777耐水性（23℃×14d）無裂紋、分層、起泡和破碎GB/T1690粘結強度/MPa≥干燥基面0.400.60GB/T16777潮濕基面0.400.60浸水處理后保持率0.400.50彈性恢復率/%≥8590GB/T23457釘桿自愈性無滲水GB23441吸水率（24h）/%≤2.0GB/T19250低溫柔性無處理-20℃，無裂紋-30℃，無裂紋GB/T16777熱處理-18℃，無裂紋、斷裂-28℃，無裂紋、斷裂酸處理-15℃，無裂紋、斷裂-25℃，無裂紋、斷裂堿處理鹽處理紫外線處理拉伸性能拉伸強度/MPa≥無處理0.600.8GB/T528斷裂伸長率/%≥無處理1000堿處理800酸處理鹽處理熱處理紫外線處理注：根據(jù)特定項目，供需雙方可以商定具體技術指標。涂速凝高分子液體橡膠防水膠膜A、B組分外觀要求應符合表4.0.2的規(guī)定。表4.0.2噴涂速凝液體橡膠A、B組分外觀要求項目A組分B組分色澤深褐色乳白色組織狀態(tài)乳液（允許有析出物）固體雜質無無不正常氣味無無A組分的環(huán)保指標須符合有害物質含量應符合JC1066《建筑防水涂料中有害物質限量》水性防水涂料A類的要求，見表4.0.3。表4.0.3環(huán)保性能指標項目有害物質限量試驗方法總揮發(fā)性有機化合物（g/L）≤80GB/T41078水性涂料游離甲醛/mg/kg≤100苯、甲苯、乙苯和二甲苯總和/mg/kg≤300氨/mg/kg≤500節(jié)點處理用胎體增強材料宜選用符合《屋面工程技術規(guī)范》GB50345附錄B.1.9要求的材料。噴涂速凝高分子液體橡膠防水膠膜與其它材料復合使用時，應符合下列規(guī)定：1相鄰材料之間應相容。不相容材料復合使用時，中間應設置隔離層，且隔離層材料與相鄰材料均應有良好的相容性；2噴涂速凝高分子液體橡膠防水膠膜的上部不得與采用有機化學溶劑涂料、熱熔法施工的防水卷材直接復合。運輸、儲存1噴涂速凝高分子液體橡膠防水膠膜應密閉包裝，容器表面應標明名稱、生產(chǎn)廠家、執(zhí)行標準、生產(chǎn)日期和產(chǎn)品的有效期。2噴涂速凝高分子液體橡膠防水膠膜的儲存和運輸應密閉保存，避免雨淋和暴曬，現(xiàn)場存放應整齊并應嚴格控制物料溫度在5℃～35℃之間，冬季應采取保溫措施，夏季應存放在陰涼干燥處或采取防曬措施。

5設計5.1一般規(guī)定噴涂速凝高分子液體橡膠防水膠膜的防水設計應包括下列內容：1防水工程的設防等級和設防要求；2噴涂速凝高分子液體橡膠防水膠膜性能及應用要求；3節(jié)點及細部構造防水設計；4防水膠膜應有保護措施。噴涂速凝高分子液體橡膠防水膠膜應設置在防水工程結構的迎水面1防水工程的設防等級和設防要求；2噴涂速凝高分子液體橡膠防水膠膜性能及應用要求；3節(jié)點及細部構造防水設計；4防水膠膜應有保護措施。5.2屋面防水工程屋面防水工程，噴涂速凝高分子液體橡膠防水膠膜采用單獨使用時，設計厚度應符合3.0.1的要求；與其他材料復合使用時，設計厚度不宜小于1.5mm，并符合GB55030的規(guī)定。屋面隔離層材料宜選用100g/m2無紡布、或0.4mm以上的聚乙烯、聚丙烯膜等。結構的陰、陽角部位宜處理成圓弧狀，陰角直徑宜大于50mm、陽角直徑宜大于10mm，并設置加強層，見圖5.2.3-1和圖5.2.3-2。圖5.2.3-1陰角處理示意圖1-基層2-加強層3-噴涂速凝高分子液體橡膠防水膠膜圖5.2.3-2陽角處理示意圖1-基層2-加強層3--噴涂速凝高分子液體橡膠防水膠膜噴涂速凝高分子液體橡膠防水膠膜在檐口部位收頭，收頭處逐漸噴薄處理或用密封膠進行密封，無組織排水檐口的防水膠膜應噴涂至檐口邊緣，見圖5.2.4。圖5.2.4檐口防水構造示意圖1-找坡層2-噴涂速凝高分子液體橡膠防水膠膜3-保護層天溝和檐溝與屋面的交接部位應設置增強層，噴涂速凝高分子液體橡膠防水膠膜應由溝底翻上至溝外側頂部。收頭處做逐漸噴薄處理或用密封膠進行密封，見圖5.2.5。圖5.2.5檐溝防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠防水膠膜4-保護層低女兒墻應增設防水加強層，泛水處的防水膠膜可直接噴涂至壓頂下，并做鋁合金壓條固定，見圖5.2.6。圖5.2.6低女兒墻防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜高女兒墻應設加強層，防水膠膜的泛水高度不應小于250mm，泛水上部的墻體應做防水處理，并做鋁合金壓條固定，見圖5.2.7。圖5.2.7高女兒墻防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜屋面變形縫中應嵌填密封材料同時增設胎體增強材料的加強層，頂部應加混凝土或金屬蓋板，其防水構造見5.2.8。圖5.2.8屋面變形縫防水構造示意圖1-填充材料2-加強層3-聚乙烯泡沫棒4-加強層5-噴涂速凝高分子液體橡膠膠膜高低跨屋面防水層與立墻交接處變形縫，應增設夾鋪胎體增強材料的加強層，縫中嵌填密封材料，并采取能適應變形的覆蓋處理。防水構造見圖5.2.9。圖5.2.9高低跨變形縫防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜4-泛水板水落口周邊500mm范圍內坡度不應小于5%，防水層下應增設加強層，防水層和加強層應伸入水落口內50mm。其防水構造見圖5.2.10。圖5.2.10水落口防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜出屋面管道應增設加強層，周圍應抹出倒角，泛水處防水層高度不應小于250mm，收頭處做逐漸噴薄處理。防水構造見圖5.2.11。圖5.2.11出屋面管道防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜5.3地下防水工程地下防水工程中，采用噴涂速凝高分子液體橡膠防水膠膜作為防水層時，防水層應設在迎水面。噴涂速凝高分子液體橡膠防水膠膜采用單獨使用時，設計厚度應符合3.0.1的要求；與其他材料復合使用時，設計厚度不宜小于1.5mm，并符合GB55030的規(guī)定。底板與立墻施工防水層連接部位甩槎與接茬構造見圖5.3.3-1、圖5.3.3-2和圖5.3.3-3。圖5.3.3-1甩槎 圖5.3.3-2接槎墊層2-噴涂速凝高分子液體橡膠膠膜3-底板結構層 1-墊層2-噴涂速凝高分子液體橡膠膠膜3-地板結構層圖5.3.3-3接槎1-墊層2-噴涂速凝高分子液體橡膠防水膠膜3-底板結構層地下工程混凝土施工縫采用噴涂速凝橡膠瀝青防水膠膜作防水層時，應采用胎體增強層對施工縫先進行加強處理，增強層在施工縫兩側向外延伸的寬度不應小于250mm，防水構造見圖5.3.4。圖5.3.4施工縫防水構造示意圖1-結構層2-加強層3-噴涂速凝高分子液體橡膠膠膜地下工程底板、頂板、側墻變形縫采用噴涂速凝高分子液體橡膠防水膠膜做防水層時，變形縫兩側應做增強層，增強層向外延伸寬度不應小于250mm，防水構造見圖5.3.5-1和圖5.3.5-2。圖5.3.5-1底板變形縫防水構造示意圖1-墊層2-噴涂速凝高分子液體橡膠防水膠膜3-結構底板圖5.3.5-2頂板及側墻變形縫防水構造示意圖1-結構層2-加強層3噴涂速凝高分子液體橡膠防水膠膜地下工程混凝土結構后澆帶接縫處噴涂速凝高分子液體橡膠防水膠膜應設置加強層，加強層兩邊均應不小于250mm。防水構造見圖5.3.6-1和圖5.3.6-2。圖5.3.6-1頂板及側墻后澆帶防水構造示意圖1-結構頂板2-加強層3-噴涂速凝高分子液體橡膠防水膠膜圖5.3.6-2底板后澆帶防水構造示意圖1-噴涂速凝高分子液體橡膠防水膠膜2-加強層3-結構底板樁頭的防水層應緊密連接，并與作為加強層的噴涂速凝高分子液體橡膠防水膠膜連接成整體。防水層應做到樁頭根部，噴涂時應對樁頭、鋼筋做遮擋保護處理，見圖5.3.7。圖5.3.7樁頭防水構造示意圖1-結構層2-噴涂速凝高分子液體橡膠防水膠膜3-加強層4-水泥基滲透結晶型防水涂料5-遇水膨脹止水膠（環(huán)）5.4地鐵及隧道防水工程隧道防水工程采取對二襯結構全部包裹的防水方式，噴涂施工前應對噴混凝土表面采用砂漿找平層，或鋪貼土工膜。噴涂速凝高分子液體橡膠防水膠膜采用單獨使用時，設計厚度應符合3.0.1的要求；與其他材料復合使用時，設計厚度不宜小于1.5mm，并符合GB55030的規(guī)定。暗挖隧道防水構造見圖5.4.3；圖5.4.3暗挖隧道防水構造示意圖1-二次襯砌2-噴涂速凝高分子液體橡膠膠膜3-土工膜4-初期支護暗挖隧道頂（拱）板側墻變形縫防水構造見圖5.4.3。圖5.4.3暗挖隧道頂（拱）板側墻變形縫防水構造示意圖1-HDPE膜2-加強層3-噴涂速凝高分子液體橡膠膠膜4-結構層暗挖隧道結構底板變形縫防水構造見圖5.4.4。圖5.4.4暗挖隧道結構底板變形縫防水構造示意圖1-底板結構2-噴涂速凝高分子液體橡膠膠膜3-HDPE膜4-墊層明挖結構防水構造見圖5.4.5-1和圖5.4.5-2圖5.4.5-1明挖結構防水構造示意圖1-底板2-噴涂速凝橡膠瀝青防水涂料3-HDPE膜4-墊層5-噴涂速凝橡膠瀝青防水涂料6-頂板7-側墻8-噴涂速凝高分子液體橡膠膠膜9-HDPE膜10-圍護結構圖5.4.5-2明挖結構防水構造示意圖1-拱墻2-噴涂速凝橡膠瀝青防水涂料3-墊層4-HDPE膜5-噴涂速凝高分子液體橡膠膠膜6-底板

6施工6.1一般規(guī)定施工單位應具備相應的專業(yè)施工資質。噴涂作業(yè)人員應經(jīng)過專門噴涂施工培訓后，才能進行操作。材料進場時，噴涂速凝高分子液體橡膠防水膠膜應有：出廠檢驗報告、合格證和性能檢測報告。材料進場后進行材料見證檢驗，合格后方可使用。施工前應對圖紙進行會審，并按設計及工程要求，編制專項防水施工方案，經(jīng)工程總包單位及監(jiān)理單位審批后執(zhí)行。施工時應對易受施工影響的作業(yè)區(qū)進行遮擋，施工時不得污染已完工的其他工序作業(yè)面及飾面?；鶎颖仨毞戏浪┕さ囊?，如不符合要求，則應進行處理，經(jīng)過驗收合格，方可進行防水施工。細部構造部位應按設計要求進行加強處理，處理措施應符合本規(guī)程第5章的要求。防水施工過程中，對工程質量應建立各道工序的自檢、并設專職人員巡視檢查制度。每道工序檢驗合格后方可進行下道工序。噴涂速凝高分子液體橡膠防水膠膜施工完畢后，檢查防水層是否有漏噴、針孔、鼓泡、剝落及損傷等缺陷，并進行修補處理。噴涂速凝高分子液體橡膠噴涂施工時，以專用噴涂設備為基點，應遵循下列原則：1基層為底（頂）板時，應遵循自遠而近的原則；2基層為立面時，應遵循自下而上的原則；3基層為斜面時，應遵循自低而高的原則；4基層為頂面時，應遵循自遠而近的原則。噴涂速凝高分子液體橡膠防水膠膜施工應符合下列規(guī)定：1施工人員應按規(guī)定佩戴、使用安全防護用品；2屋面施工時，屋面周邊和預留孔洞應設置安全防護欄和安全網(wǎng)或其他防止墜落措施；3施工環(huán)境溫度宜為5℃～40℃。雨天、雪天、五級風以上天氣不宜實施露天噴涂作業(yè)；4冬季施工應對A組分和B組分采取保溫措施。6.2基層處理基層可以潮濕，但須干凈、堅實、無明水，表面平整度應符合相關規(guī)范要求。各種預埋管件、設備基礎、預留洞口等均應在防水層施工前埋設和安裝牢固，并驗收合格。所有陰角處須抹成八字角。6.3施工準備材料準備 噴涂速凝高分子液體橡膠防水膠膜由A組份和B組份組成。噴涂前使用攪拌器對A組份進行充分攪拌，攪拌方法見廠家產(chǎn)品說明書，將B組份在配料桶內按照比例配置好，待用。設備與機具1施工主設備：專用噴涂機、高壓軟管、噴槍及配套設備；2其他機具：攪拌器，配料桶、金屬過濾網(wǎng)、工具箱等；3輔助材料：常用清理及抹灰工具，水桶，掃帚，剪刀等；4防護設備：防護服，安全帽，護目鏡，安全帶、乳膠手套等。噴涂設備調試應符合下列規(guī)定，合格后方可施工；1啟動前連接高壓軟管和噴槍，并檢查汽油、是否達到規(guī)定的油面，泵體閥門開關是否在關閉狀態(tài)：2啟動發(fā)動機處于怠速狀態(tài)，檢查發(fā)動機工作是否正常，確保各連接裝置無滲（滴）漏；3開啟閥門開關，在調試桶內調試噴槍噴涂流量，檢查有無堵塞和不暢；4正式噴涂施工前應進行試噴，將噴涂料噴涂在硬紙板上，調整噴涂距離，觀察涂層固化是否正常，合格后正式噴涂；5噴涂施工作業(yè)完畢，應清理噴涂設備，確認清洗干凈后關機；6剩余物理應集中收集，妥善處理廢物。6.4噴涂施工噴涂施工的工藝流程噴涂速凝高分子液體橡膠防水膠膜噴涂施工時應按下列工藝流程施工：機具準備、機具準備、材料準備基層處理交接驗收修整自檢修整細部施工自檢修整噴涂施工成品驗收成品養(yǎng)護成品保護層局部加強處理：按設計要求，在結構陰陽角、穿墻管根、施工縫、泛水、落水口等節(jié)點、細部構造部位噴涂增強層。增強層采用胎體增強材料時，防水涂料應充分浸透胎體增強材料，不得有露槎。噴涂作業(yè)時，噴槍宜垂直于噴涂基層，距離適中，均勻移動。應按照先細部構造后整體噴涂的順序連續(xù)作業(yè)，一次多遍、交叉噴涂達到設計要求的厚度。在里面或坡面施工時，噴槍應按照自下而上，由低到高的順序噴涂，不得漏噴。大面施工時，噴涂施工宜分段分區(qū)完成，每個分區(qū)以500m2～1000m2為宜。相鄰區(qū)域噴涂的搭接寬度不應小于100mm。如搭接處有浮漿、灰塵、油污等雜物，應進行清潔處理后可繼續(xù)噴涂。噴涂速凝高分子液體橡膠防水膠膜噴涂施工完成后，在下道工序施工前，應進行自檢，必要時，要進行修補。6.5搭接和甩槎的操作方法平面甩茬：兩次噴涂搭接長度不應少于100mm，對30cm的預留部分邊緣部位以隔離膜上壓磚遮蓋進行保護，保護層不能蓋過甩槎處。再次噴涂時，先去除隔離膜及磚，噴涂搭接部位并進行后續(xù)施工。外防外貼側墻甩槎：外側墻噴涂速凝高分子液體橡膠防水膠膜操作順序應遵循為自下而上操作的原則。噴涂時與立墻緊密粘接，不竄水，不剝離，無需甩茬，不存在像卷材防水層墜落的現(xiàn)象。操作過程中注意鋪設起保護層作用的聚苯板不能遮蓋已經(jīng)噴涂的防水膠膜的作業(yè)面上端。待回填后，在防水膠膜界面上端繼續(xù)噴涂（第二次噴涂時，不論間隔多長時間，在原液體橡膠防水層上直接噴涂，不需要做任何處理）。外防內貼時，如側墻平整，可直接噴涂噴涂速凝高分子液體橡膠防水膠膜。噴涂高度應高于后澆混凝土50cm以上。如側墻不平整時，可采用懸掛100g無紡布，配置梅花釘?shù)姆绞?，在無紡布上噴涂噴涂速凝高分子液體橡膠防水膠膜，噴涂高度應高于后澆混凝土50cm以上。磚胎膜甩槎：a.在磚胎膜內側及上部進行噴涂噴涂速凝高分子液體橡膠防水膠膜，按增強層處理；b.在磚胎膜上部加一層隔離膜并壓磚對已噴涂的表面上進行保護；c.待澆筑完立墻后，噴涂側墻防水至磚胎膜上端；d.去除磚胎膜上的磚和隔離膜；e.在磚胎膜和側墻上噴涂噴涂速凝高分子液體橡膠防水膠膜，使之形成一個整體防水層。6.6保護層施工噴涂速凝高分子液體橡膠防水膠膜施工質量檢查驗收合格后，應按設計要求及時進行保護層施工。當保護層設計為剛性保護層時，保護層施工不得破壞噴涂速凝高分子液體橡膠防水膠膜。保護層應符合下列規(guī)定：1頂板防水層應做細石混凝土保護層，并宜設置分格縫，保護層厚度應符合下列規(guī)定：（1）采用機械碾壓回填土時，保護層厚度不宜小于70mm；（2）采用人工回填土時，保護層厚度不宜小于50mm；（3）防水層與保護層之間應設置隔離層。2底板防水層宜設置厚度不小于50mm厚的混凝土保護層；3側墻防水層的保護層宜采用砌體保護，也可采用厚度不宜小于30mm的擠塑聚苯板保護。

7工程驗收7.1一般規(guī)定噴涂速凝高分子液體橡膠防水膠膜防水層的基面應進行專項驗收。噴涂速凝高分子液體橡膠防水膠膜防水層施工完成后應做單項驗收。噴涂速凝高分子液體橡膠防水膠膜防水層的最小厚度不得小于設計厚度的90%。噴涂速凝高分子液體橡膠防水膠膜防水層應密實、連續(xù)、粘接牢固，無開裂、脫落等缺陷。噴涂速凝高分子液體橡膠防水膠膜防水工程驗收時應提交下列資料：1工程防水的設計文件，圖紙會審、設計變更、洽商記錄單；2產(chǎn)品合格證、質量檢驗報告、進場抽樣復驗報告；3施工方案及安全、技術交底文件；4隱蔽工程驗收記錄；5現(xiàn)場防水滲漏檢驗記錄；6施工記錄和施工質量檢驗記錄；噴涂速凝高分子液體橡膠防水膠膜材料進場后進行見證取樣復檢，復檢項目按表7.1.6進行，若材料中有兩項或兩項以上項目檢驗結果不符合標準規(guī)定，則判定該批材料性能不合格。當材料中僅有一項檢驗結果不符合標準規(guī)定，允許在同批材料中重新取樣對該項進行復檢，復檢結果符合規(guī)定時，則判定該批材料物理性能合格，否則判為不合格。進場抽樣復檢材料，以同一生產(chǎn)時間數(shù)量為一個批次為40t。表7.1.6進場抽樣復檢項目項目指標屋面工程地下工程固體含量/%≥5555耐熱度/℃無流淌、滑動、滴落120±290±2不透水性，0.3Mpa120min不透水-膠膜抗?jié)B性，0.3Mpa-120min無滲水斷裂伸長率，%≥1000≥800低溫柔性-25℃，不斷裂-20℃，不斷裂檢驗批次：1屋面工程宜按屋面面積每2000m2劃分為一個檢驗批，不足2000m2應按一個檢驗批；每1000m2抽查3處；2地下工程宜按屋面面積每10000m2劃分為一個檢驗批，不足10000m2應按一個檢驗批；每1000m2抽查3處；3廚房、衛(wèi)生間、水池等以每一個自然間或每一個水池為一個檢驗批，逐一檢驗；4其他防水工程參照上述規(guī)定。7.2主控項目屋面防水層1屋面防水膠膜應符合設計要求和本規(guī)程的規(guī)定。檢驗數(shù)量：2000m2檢驗方法：檢查材料出廠合格證、質量檢驗報告和進場抽樣復驗報告。2屋面防水層不得有滲漏和積水現(xiàn)象。檢驗數(shù)量：2000m2檢驗方法：雨后觀察或淋水2h、蓄水24h檢測。3防水膠膜的平均厚度應符合設計要求和本規(guī)程的規(guī)定，且最小厚度不得小于設計厚度的90%。檢查數(shù)量：2000m2。檢驗方法：采用針測法檢測。4防水膠膜在天溝、檐溝、女兒墻、水落口、管根、變形縫、施工縫及后澆帶等節(jié)點、細部構造防水措施應符合設計要求和本規(guī)程的規(guī)定。檢查數(shù)量：單一部位。檢驗方法：觀察檢查和檢查隱蔽工程驗收記錄。地下工程防水層1噴涂速凝高分子液體橡膠防水膠膜地下工程防水層應符合設計要求和本規(guī)程的規(guī)定。檢查數(shù)量：10000m2。檢驗方法：檢查材料出廠合格證、質量檢驗報告和進場抽樣復驗報告。2膠膜防水層的平均厚度應符合設計要求和本規(guī)程的規(guī)定，且最小厚度不得小于設計厚度的90%。檢查數(shù)量：10000m2。檢驗方法：用針測法檢查3噴涂速凝高分子液體橡膠在陰陽角、變形縫、施工縫、穿墻管等節(jié)點部位做法必須符合設計要求。檢查數(shù)量：單一部位。檢查方法：觀察檢查和檢查隱蔽工程驗收記錄。7.3一般項目噴涂速凝高分子液體橡膠防水膠膜與基面應粘接牢固，膠膜表面平整、均勻，不得流淌、皺折、翹邊缺陷。檢查數(shù)量：10000m2。檢驗方法：觀察檢查。膠膜防水層應連續(xù)、無縫隙、無漏噴、無滴落、不流淌。檢查數(shù)量：10000m2。檢驗方法：觀察檢查。防水膠膜的保護層應符合設計要求。檢查數(shù)量：10000m2。檢驗方法：觀察檢查。

8安全和環(huán)境保護8.1成品保護噴涂速凝高分子液體橡膠防水膠膜施工時應注意遮擋非工作面，不得污染其他工序及飾面。噴涂速凝高分子液體橡膠防水膠膜施工后不得受重物或尖銳物沖擊，不得在已完工的防水層上鑿眼打洞，破壞膠膜。噴涂速凝高分子液體