不同煉鋼爐的爐型所排出的鋼渣的化學(xué)成份，%鋼渣的化學(xué)成分SiO2Al2O3Fe2O3CaOMgOTiO2R2OP2O5SO3ClMnO杭鋼21.507.463.9455.575.450.000.62.170.0110.420首鋼15.285.3118.5543.1512.391.060.060.920.101.12柳鋼14.864.105.7952.308.501.300.421.90鋼渣的基本情況不同鋼廠的鋼渣化學(xué)成份，%產(chǎn)地SiO2Fe2O3Al2O3CaOMgOFeOMnOP2O5f-CaO堿度首都鋼鐵公司14.8610.373.8844.0010.0412.301.111.311.802.72本溪鋼鐵公司15.9912.293.0040.509.227.341.340.562.802.45唐山鋼鐵公司15.3812.732.5440.309.0514.061.881.101.842.45太原鋼鐵公司14.228.792.8647.809.2913.291.060.561.573.13鞍山鋼鐵公司15.4310.712.4439.2911.0416.481.270.742.022.43馬鞍山鋼鐵公司11.486.472.1041.297.2615.831.791.0612.773.29南京鋼廠17.197.431.4840.148.7916.941.991.514.312.15韶鋼18.387.463.0440.773.1415.495.381.278.572.07我國部分鋼鐵廠轉(zhuǎn)爐鋼渣的化學(xué)成分%

鋼渣的基本情況主要礦物：有硅酸二鈣C2S、硅酸三鈣C3S；RO相、薔薇輝石C3RS2、橄欖石CRS、鐵酸二鈣C2F、鐵酸鈣CF、游離氧化鈣(f-CaO)、游離氧化鎂(f-MgO)，有的鋼渣中還會(huì)出現(xiàn)黃長石C2AS、尖晶石等。鋼渣的基本情況●鋼渣中含有5~15%的金屬鐵和14~30%的含鐵磁性物質(zhì)；●早期治渣的目的：提取廢鋼10%，90%尾渣廢棄；●濟(jì)鋼集團(tuán)用2-Φ2.2×7.0球磨機(jī)，2006年年處理含鐵量30％鋼渣l0萬噸，可產(chǎn)出產(chǎn)TFe>95％的粒鋼0．75萬噸，TFe>65％的鐵精粉1．75萬噸；比表面積>420mVkg的鋼渣微粉7．5萬噸。鋼渣的含鐵情況TFeFe2O3FeOSiO2Ai2O3CaOMgOMnOP2O5堿度硬度容重30.154.168．5015.913.9840.142.855.200.782.49~101.6鋼渣的易磨性試樣種類

密度,g/cm3水分,%粉磨功指數(shù),kWh/t磨蝕性指數(shù),g水淬鋼渣3.480.7723.6(P=80μm)大塊鋼渣3.640.1229.3(P=80μm)0.4762（砂巖類0.4020水泥熟料0.1389）礦渣2.891.1423.5(P=80μm)鋼渣的基本情況●杭鋼鋼渣粉磨功指數(shù)Wi=23.1kW·h/t

●首鋼鋼渣的粉磨功指數(shù)Wi

=19.4kW·h/t●礦渣的平均粉磨功指數(shù)21.3kW·h/t●熟料的平均粉磨功指數(shù)15.9kW·h/t

●石灰石的平均粉磨功指數(shù)11.0kW·h/t

唐山嘉恒實(shí)業(yè)有限公司的鋼渣/礦渣試樣樣品SiO2Al2O3Fe2O3CaOMgOTiO2K2ONa2OSO3合量易磨性電爐渣15.804.9543.8728.206.680.050.100.2796.8824.7連鑄渣14.5617.5113.9441.217.330.700.050.061.9997.6127.4天津（大無縫）鋼管廠鋼渣試樣說明：連鑄渣含5%的金屬鐵塊，因無法破碎，所以在制樣時(shí)剔除，破碎后又用磁鐵吸除鐵渣?！窕厥諒U鋼：一些煉鋼企業(yè)，也在開發(fā)渣山中回收了大量廢鋼；●作為冶金原料：利用鋼渣中含有很高的CaO、鐵分以及一定比例的MgO、MnO等能夠有效降低熔劑、礦石的消耗及能耗的組分，將鋼渣制成球后返回?zé)掍摖t作為熔劑使用；●在基建中的使用：利用鋼渣的容重大、呈塊狀、表面粗糙、不滑移、強(qiáng)度高、耐磨、耐蝕、與瀝青粘結(jié)牢固等特點(diǎn)，在交通道路方面、海港碼頭、工廠住宅區(qū)等建設(shè)中，使用了大量鋼渣用作筑路的基材或回填料等；●在農(nóng)業(yè)方面的應(yīng)用：鋼渣富含鈣、鎂、磷、硅和少量錳、鋅和銅等，具有多種農(nóng)作物的營養(yǎng)元素，在鋼渣的綜合利用中，農(nóng)業(yè)上的施用是有效利用的重要途徑之一；●在水泥工業(yè)中的應(yīng)用：鋼渣在水泥工業(yè)中的應(yīng)用主要包括配燒水泥熟料和作為水泥或混凝土的混合材來使用。鋼渣的利用途徑鋼渣的基本情況鋼渣的基本特點(diǎn)（總結(jié)）●成分和活性波動(dòng)較大：因?yàn)殇摰钠贩N、原料來源和煉鋼出渣工藝的不同，鋼渣的成分和活性波動(dòng)較大；●對(duì)混凝土有害成分：游離氧化鈣(f-CaO)、游離氧化鎂(f-MgO)水化后容易引起混凝土體積膨脹；●含鐵量高：鋼渣中含有5~15%金屬鐵和14~30%的含鐵磁性物質(zhì)，對(duì)破碎和粉磨部件的磨損比較嚴(yán)重；●易磨性差：平均易磨性25kWh/t左右。鋼渣的基本情況鋼渣水泥系列標(biāo)準(zhǔn)序號(hào)標(biāo)準(zhǔn)名稱標(biāo)準(zhǔn)號(hào)1鋼渣硅酸鹽水泥GB

13590-20062鋼渣道路水泥JC/T1087-20083低熱鋼渣水泥JC/T1082-20084鋼渣砌筑水泥JC/T

1090-20085用于水泥的鋼渣YB/T

022-20086用于水泥和混凝土中的鋼渣粉GBT

20491-20067水泥用鋼渣化學(xué)分析方法YB/T

140-19988水泥用鋼渣中金屬鐵含量測定方法YB/T

148鋼渣微粉的性能研究在利用鋼渣生產(chǎn)水泥方面，中國起步較早，二十世紀(jì)六十年代，我國就開始用鋼渣生產(chǎn)水泥的研究并投入生產(chǎn)，目前已經(jīng)制定了一系列鋼渣水泥標(biāo)準(zhǔn)?！幸苯ㄖ芯靠傇河邢薰卷?xiàng)目級(jí)別350級(jí)450級(jí)750級(jí)比表面積（m2/kg）350±50450±50750±50密度（kg/m3）3.15±0.153.15±0.152.80±0.20游離CaO含量（％）≤3.0≤3.0≤3.0金屬鐵含量（％）≤0.8≤0.8≤0.8堿含量（％）≤0.3≤0.3≤0.3水含量（％）≤2.0≤2.0≤2.0堿度系數(shù)≥2.0≥2.0≥2.0活性指數(shù)（％）7天≥75≥80≥8528天≥80≥85≥90流動(dòng)度比（％）≥100≥100≥100安定性如果MgO含量大于13％，則應(yīng)在525硅酸鹽水泥中摻加30％后，經(jīng)壓蒸法檢驗(yàn)合格鋼渣微粉標(biāo)準(zhǔn)（舊）鋼渣微粉的性能研究鋼渣的堿度M＝鋼渣微粉標(biāo)準(zhǔn)（新）——用于水泥和混凝土中的鋼渣粉中鋼渣粉的技術(shù)要求項(xiàng)

目級(jí)

別一級(jí)二級(jí)比表面積，m2/kg≥400密度，g/cm3≥2.8含水量，%≤1.0f-CaO含量(質(zhì)量分?jǐn)?shù))，%≤3.0SO3含量(質(zhì)量分?jǐn)?shù))，%≤4.0堿度系數(shù)≥1.8活性指數(shù)，%7d≥65≥5528d≥80≥65流動(dòng)度比，%≥90安定性沸煮法合格壓蒸法當(dāng)鋼渣中MgO含量大于13%時(shí)應(yīng)檢驗(yàn)合格鋼渣微粉的性能研究●不同比表面積水淬鋼渣粉的物理性能試驗(yàn)結(jié)果樣品水鋼流動(dòng)鋼渣粉需水抗折強(qiáng)度抗壓強(qiáng)度安編號(hào)泥渣度比表面積量7d28d7d28d定ggmmm2/kg%MPa活性%MPa活性%MPa活性%MPa活性%性B04500190+19033327.207.2100.009.05100.0047.3100.0060.2100.00合格B01315135190+19539126.565.474.887.482.1428.259.6250.684.04合格B1315135190+19542326.625.576.047.683.9829.562.3752.086.38合格B2315135190+19045526.705.069.127.381.0328.059.1551.986.15合格B3315135195+19547926.704.967.747.279.5627.357.6950.684.03合格B4315135195+19550826.604.662.907.785.0824.451.5949.982.95合格B5315135190+18560726.604.562.566.976.4324.952.7048.580.49合格B4'315135210+2055084.664.0622.447.33R1315135185+1804224.765.447.784.7126.155.1150.383.51合格R2315135195+1954434.662.907.683.9824.651.9949.682.45合格R3315135190+19549126.964.764.527.077.1624.451.4846.977.98合格R4315135190+1855184.561.527.481.7724.451.5048.680.71合格R5315135215+2106005.271.207.178.0826.556.0251.385.26合格鋼渣微粉的性能研究唐山嘉恒實(shí)業(yè)有限公司的鋼渣/礦渣試驗(yàn)結(jié)果●水淬鋼渣粉與礦渣粉組成的復(fù)合粉的活性樣品編號(hào)水泥g水淬鋼渣g礦渣g復(fù)合粉比表面積m2/kg抗折強(qiáng)度抗壓強(qiáng)度安定性7d28d7d28dMPa活性%MPa活性%MPa活性%MPa活性%SS131567.5067.504105.979.828.492.6331.467.2457.795.91合格SS231567.5067.504416.081.868.290.9832.369.1056.193.24合格SS331587.7547.256.081.868.189.13%34.072.8956.193.16%合格SS431547.2587.756.993.889.3103.04%36.277.4659.799.08%合格S131501354026.487.538.998.0135.976.8162.6104.01合格鋼渣微粉的性能研究樣品編號(hào)水淬礦渣熟料石需水凝結(jié)時(shí)間抗折強(qiáng)度抗壓強(qiáng)度安定性鋼渣粉粉粉膏量初凝終凝3d28d增進(jìn)率3d28d增進(jìn)率%%%%%h:minh:minMPaMPa28d/3dMPaMPa28d/3d13252106＞12＞120.37.616.181.037.435.94合格2324220627.9212:29＞120.67.56.803.140.412.96合格3323230627.659:2711:251.06.34.275.634.56.17合格4322240627.297:319:002.36.82.929.338.84.16合格5321250627.206:007:172.86.92.5013.243.73.30合格632260626.665:006:083.77.11.9116.542.92.61合格●鋼渣/礦渣粉配制水泥的有關(guān)性能濟(jì)鋼集團(tuán)2006年的試驗(yàn)結(jié)果試驗(yàn)次數(shù)編號(hào)組成／％抗折強(qiáng)度抗壓強(qiáng)度水泥鋼渣粉礦渣粉3d7d28d3d7d28d第一次試驗(yàn)P.I100006.38.59.331.446.770.6G3703003.56.58.116.237.153.6K3700305.16.98.721.635.961.5KG37010205.07.09.022.437.561.9K5500503.25.38.214.825.855.6KG55015352.95.28.112.526.152.4第二次試驗(yàn)P.I100005.87.810.128.650.272.1G3703003.96.27.816.133.858.4K3700304.36.38.619.335.366.3KG37010204.36.38.819.434.864.4K5500503.25.18.913.125.557.7KG55015352.64.87.810.824.752.5鋼渣微粉的性能研究試樣名稱密度，g/cm3比表面積，m2/kg鋼渣微粉3.25~3.35486.4礦渣微粉2.88~2.90478.7通用硅酸鹽水泥標(biāo)準(zhǔn)品種代號(hào)熟料+石膏混合材燒失量細(xì)度凝結(jié)時(shí)間硅酸鹽水泥P.I1000≤3.0≥300m2/kg初≥45min終≤390minP.II≥95礦渣或石灰石≤5≤3.5普通硅酸鹽水泥P.O80~955~20≤5.0初≥45min終≤600min礦渣硅酸鹽水泥P.S.A50~8020~50R80mm＜10%或R45mm＜30%P.S.B30~5050~70火山灰硅酸鹽水泥P.P60~80火山灰質(zhì)20~40粉煤灰硅酸鹽水泥P.F60~80粉煤灰20~40復(fù)合硅酸鹽水泥P.C50~8020~50鋼渣微粉的性能研究水泥的強(qiáng)度性能指標(biāo)品種強(qiáng)度等級(jí)抗壓強(qiáng)度抗折強(qiáng)度3d28d3d28d硅酸鹽水泥42.5≥17.0≥42.5≥3.5≥6.542.5R≥22.0≥4.052.5≥23.0≥52.5≥4.0≥7.052.5R≥27.0≥5.062.5≥28.0≥62.5≥5.0≥8.062.5R≥32.0≥5.5普通硅酸鹽水泥42.5≥17.0≥42.5≥3.5≥6.542.5R≥22.0≥4.052.5≥23.0≥52.5≥4.0≥7.052.5R≥27.0≥5.0復(fù)合硅酸鹽水泥礦渣硅酸鹽水泥火山灰硅酸鹽水泥粉煤灰硅酸鹽水泥32.3≥10.0≥32.5≥2.5≥5.532.5R≥15.0≥3.542.5≥15.0≥42.5≥3.5≥6.542.5R≥19.0≥4.052.5≥21.0≥52.5≥4.0≥7.052.5R≥23.0≥4.5鋼渣微粉的性能研究鋼渣粉作為水泥活性混合材的試驗(yàn)結(jié)果1、鋼渣粉的細(xì)度要求：比表面積≥380m2/kg2、水泥的性能指標(biāo)：★石膏摻量控制SO3在1.8～2.2％；★凝結(jié)時(shí)間符合一般混合材的影響規(guī)律；★標(biāo)準(zhǔn)稠度無影響，完全正?！锪鲃?dòng)度略有改善，有所提高★安定性水泥的壓蒸安定性合格陳益民博士（中國建筑材料科學(xué)研究院）

1999年開始《水泥和混凝土用高活性摻合料的磨細(xì)鋼渣粉》項(xiàng)目研究：使用磨細(xì)鋼渣粉可替代10％~45％的425#和525#水泥，配制C20~60高強(qiáng)度混凝土。每使用1噸磨細(xì)鋼渣粉，可降低成本100元，并提高混凝土強(qiáng)度10％左右。鋼渣微粉的性能研究鋼渣粉作為混凝土活性摻合料的試驗(yàn)結(jié)果●鋼渣粉是一種性能優(yōu)越的混凝土摻合料，在混凝土中摻加10～35％的磨細(xì)礦渣粉，同時(shí)摻入0～20％磨細(xì)鋼渣粉和0～9％硅灰，取代10～50％的水泥，膠凝材料總用量在380～550kg/m3，可以配置C20～C60混凝土?！皲撛劭梢詥为?dú)摻入混凝土中，也可以與礦渣粉、粉煤灰、硅灰等復(fù)合摻入混凝土中。鋼渣單獨(dú)摻入時(shí)，以25％左右的鋼渣粉代替水泥時(shí)混凝土的強(qiáng)度最高。鋼渣粉對(duì)于混凝土的后期強(qiáng)度增長更為有利?！駬绞卒撃ゼ?xì)鋼渣粉的混凝土強(qiáng)度高于摻一級(jí)粉煤灰的混凝土；與摻磨細(xì)礦渣粉的混凝土相當(dāng)。●摻加首鋼磨細(xì)礦渣粉的混凝土強(qiáng)度符合一般的混凝土強(qiáng)度規(guī)律，因此，摻磨細(xì)鋼渣粉的混凝土配比設(shè)計(jì)完全可以按照通常方法和規(guī)范來進(jìn)行。●摻鋼渣粉的混凝土坍落度損失較小，也與外加劑有關(guān)?！駬饺胧卒摰哪ゼ?xì)鋼渣粉可以大大降低膠凝材料的水化熱，其降低水化熱效果與單獨(dú)摻粉煤灰時(shí)相當(dāng)，優(yōu)于礦渣粉。鋼渣微粉的性能研究試驗(yàn)1：膠凝材料總量固定—不同摻量的配合比和強(qiáng)度混凝土強(qiáng)度設(shè)計(jì)等級(jí)：C40、C50膠凝材料總量——固定：514kg/m3新港普通水泥525#：383m2/kg鋼渣粉比表面積：450m2/kg鋼渣粉摻量——調(diào)整：10～35％1、四個(gè)配合比的28天強(qiáng)度均高于55MPa；2、鋼渣粉摻量在15％～25％范圍內(nèi)，隨摻量增加，7天強(qiáng)度幾乎不變，但是28天強(qiáng)度持續(xù)增加；當(dāng)鋼渣粉取代量為25％時(shí)，強(qiáng)度最高；3、鋼渣粉摻量超過25％時(shí)，強(qiáng)度隨摻量增加而降低；當(dāng)鋼渣粉取代量為35％時(shí)，7天強(qiáng)度顯著降低，28天強(qiáng)度降低到與摻15％鋼渣粉時(shí)的強(qiáng)度相同；結(jié)論：混凝土摻入適量的磨細(xì)鋼渣粉作為摻合料，有利于提高混凝土強(qiáng)度，尤其是提高后期強(qiáng)度。鋼渣微粉的性能研究試驗(yàn)2：摻30％鋼渣粉的混凝土配合比和強(qiáng)度混凝土強(qiáng)度等級(jí)：C20～C40膠凝材料總量：調(diào)整510～310kg/m3新港普通水泥425#：m2/kg鋼渣粉比表面積：450m2/kg鋼渣粉摻量——固定30%1、混凝土強(qiáng)度在C20～C40之間，隨膠凝材料用量的增加和水/膠比的降低，混凝土的強(qiáng)度提高；2、對(duì)于摻入30％磨細(xì)鋼渣粉的混凝土；水泥本身強(qiáng)度對(duì)混凝土強(qiáng)度的影響不如水膠比的影響大；鋼渣微粉的性能研究試驗(yàn)3：復(fù)合摻加鋼渣粉和礦渣粉的混凝土試驗(yàn)

混凝土配合比中同時(shí)摻鋼渣粉和礦渣粉混凝土強(qiáng)度等級(jí)：C20～C50鋼渣粉比表面積：380～460m2/kg礦渣粉比表面積：400m2/kg1、復(fù)合摻入適量的磨細(xì)鋼渣粉和礦渣粉，可以配置出C20～C55混凝土。2、410kg/m3膠凝材料中摻入35％磨細(xì)鋼渣粉（比表面積380m2/kg），28天強(qiáng)度達(dá)到39MPa，可以配置出C30混凝土。鋼渣微粉的性能研究試驗(yàn)3分析1：配置C40混凝土

1、膠凝材料總量440～480kg/m3、摻合料總量50％（其中鋼渣粉25％），可以配置C40和C45混凝土。2、比較而言（4-1、4-3與4-5），7天強(qiáng)度隨著膠凝材料總量的增加而提高；28天強(qiáng)度460kg/m3比440kg/m3的低，是因?yàn)殇撛奂?xì)度的影響。3、膠凝材料總量500kg/m3、摻合料總量70％（其中鋼渣粉35％），頁可以配置C40混凝土。鋼渣微粉的性能研究試驗(yàn)3分析2：配置C30、C35混凝土

1、膠凝材料總量410kg/m3、單獨(dú)摻鋼渣粉（比表面積380m2/kg）35％，可以配置C30混凝土；2、膠凝材料總量440~455kg/m3，可以配置C30、C35混凝土。★總的來說，用普通425＃水泥摻加50～70％鋼渣粉和礦渣粉，不難配置出C30～C40混凝土，水泥用量非常低，對(duì)于降低大體積混凝土的溫升十分有利。鋼渣微粉的性能研究試驗(yàn)3分析3：配置C30、C35混凝土結(jié)論：膠凝材料總量400kg/m3、單獨(dú)摻鋼渣粉（比表面積380m2/kg）50％，可以配置C20混凝土。試驗(yàn)3分析4：配置C50、C55混凝土結(jié)論：1、膠凝材料總量540kg/m3、摻合料總量50％(其中鋼渣粉25％)，可以配置C50混凝土。

2、膠凝材料總量540～581kg/m3、摻合料總量33.4％(其中鋼渣粉16.7％)，可以配置C55混凝土。

鋼渣微粉的性能研究試驗(yàn)4：鋼渣粉與一級(jí)粉煤灰效果對(duì)比的混凝土試驗(yàn)

混凝土強(qiáng)度等級(jí)：C20～C60；鋼渣粉比表面積：450m2/kg；一級(jí)粉煤灰：1.設(shè)計(jì)為C25的混凝土（膠凝材料總量384kg/m3）：摻鋼渣粉30.7％的28天強(qiáng)度比摻30.7％粉煤灰的混凝土高1.2MPa；2.設(shè)計(jì)為C35的混凝土（膠凝材料總量415kg/m3）：摻鋼渣粉20％的28天強(qiáng)度比摻17.6％粉煤灰的混凝土高1.5MPa；3.設(shè)計(jì)為C40的混凝土（膠凝材料總量508kg/m3）：摻鋼渣粉20％的28天強(qiáng)度比摻15.8％粉煤灰的混凝土高2.5Mpa.鋼渣微粉的性能研究鋼渣微粉的基本特性（總結(jié)）●鋼渣粉磨至4000~5000cm2/g時(shí)可以達(dá)到二級(jí)或一級(jí)粉的要求，與鋼渣本身的性能關(guān)系較大，靠提高比表面積增加活性意義不大；●鋼渣粉摻量30%時(shí)可以配置42.5級(jí)別的水泥；與礦渣粉復(fù)合使用時(shí)活性發(fā)揮更好；●鋼渣粉是一種性能優(yōu)越的混凝土摻合料，在混凝土中摻加10～35％的磨細(xì)礦渣粉，同時(shí)摻入0～20％磨細(xì)鋼渣粉和0～9％硅灰，取代10～50％的水泥，膠凝材料總用量在380～550kg/m3，可以配置C20～C60混凝土?！駬戒撛鄣幕炷撂涠葥p失較小；磨細(xì)鋼渣粉可以幅度降低膠凝材料的水化熱。鋼渣微粉的性能研究◆“治渣王”冀更新：武漢冶金渣環(huán)保工程有限責(zé)任公司

φ1.83球磨機(jī)產(chǎn)量2t/h→6t/h“鋼渣濕法磁選分級(jí)”及“鋼渣綜合利用方法”2003年獲得國家專利

2004年底已形成年產(chǎn)11萬噸磨細(xì)鋼渣粉的生產(chǎn)能力，每噸按175元計(jì)算，產(chǎn)值達(dá)1925萬元，可創(chuàng)利800萬元。2006底將形成年處理鋼渣150萬噸的生產(chǎn)能力◆濟(jì)鋼集團(tuán)：先將鋼渣(水分<8％)預(yù)破碎，使其粒度<60mm，再進(jìn)行粉碎、磁選、篩分，得中粉，最后入磨粉磨，分級(jí)，得到≥400m3／kg微粉。每噸鋼渣粉經(jīng)生產(chǎn)線加工處理后可收益274．4元／t；其中：所產(chǎn)鋼渣微粉的收入100元/t×0.79=79元/t；鐵精粉收入720元／t×0．145=104．4元／t；顆粒鋼收入1400元／t×0．065=91元／t

鋼渣粉的單位處理成本為：耗電費(fèi)用：87kWh／t×0.5元/kWh=43.5元/t；工資福利費(fèi)用17.8元/t（33人計(jì))；備品備件、材料和介質(zhì)費(fèi)用11．1元／t；固定資產(chǎn)折舊費(fèi)用：2.3元／t；管理費(fèi)用2.45元／t；原料運(yùn)輸費(fèi)2．5元／t；原料費(fèi)用100元／t。總計(jì)為：179.65元／t。實(shí)際鋼渣處理效益為：274．4元／t-179．65元/t=94.75元／t。

鋼渣的粉磨加工研究

序號(hào)物料種類產(chǎn)量kg/h主機(jī)電耗kWh/t產(chǎn)量kg/h成品質(zhì)量比表面m2/kgR80％R45％1水淬鋼渣52.786267391.30.643.20241.577058422.90.482.70332.268647479.00.402.00418.1314528665.50.281.705水淬鋼渣：水渣=1：148.186859425.60.723.006水渣69.295081361.8鋼渣的粉