鋁塑膜檢驗(yàn)報(bào)告

外觀規(guī)定：不容許有針孔、異物、粘連、涂層不均勻、復(fù)合層間分離及明顯損傷、氣泡、皺紋、臟物等缺陷。檢查效果：合格外觀圖片測(cè)試厚度供應(yīng)商原則：測(cè)試數(shù)據(jù)0.113um(±公差10%）實(shí)測(cè)/um 上海邁恩新鋁塑膜深圳彭寶圓鋁塑膜0.1120.1110.1130.1140.1150.1120.1130.1150.1140.113均值/um0.11340.113成果OKOK實(shí)際測(cè)試成果：檢查效果：合格冷沖壓成型性試驗(yàn)方案：按規(guī)定型號(hào)設(shè)計(jì)深度沖膜不容許分層、破裂、針孔漏光項(xiàng)目方案1方案2鋁塑膜廠家上海鋁塑膜深圳鋁塑膜設(shè)計(jì)深度4.0/3.04.0/3.0模具8057080570試驗(yàn)材料輔料上海鋁塑膜試驗(yàn)數(shù)據(jù)槽深項(xiàng)目沖殼深度設(shè)備參數(shù)平均值5.0壓力沖殼時(shí)間拉伸時(shí)間最小值4.80.75Mpa0.8S最大值5.3深圳鋁塑膜試驗(yàn)數(shù)據(jù)槽深項(xiàng)目沖殼深度設(shè)備參數(shù)平均值5.0壓力沖殼時(shí)間拉伸時(shí)間最小值4.80.75Mpa0.8S最大值5.3沖壓后圖片檢查效果：按規(guī)定型號(hào)設(shè)計(jì)深度沖膜無分層、破裂、針孔漏光，經(jīng)檢查合格。耐電解液浸泡試驗(yàn)試驗(yàn)方案：溫度45℃用電解液浸泡48小時(shí)1.不容許鋁層以PP分層鋁層導(dǎo)通；2.尼龍層以鋁層分層后鋁層不能變色。里層圖片外層圖片檢查效果：PP層無分層檢查不導(dǎo)通檢查合格熔膠試驗(yàn)試驗(yàn)方案：撕開封接處，鋁塑膜兩邊粘有均勻CPP并帶乳白色封口試驗(yàn)數(shù)據(jù)：上海鋁塑膜深圳鋁塑膜設(shè)備參數(shù)設(shè)備參數(shù)項(xiàng)目頂封驗(yàn)證效果項(xiàng)目頂封驗(yàn)證效果壓力0.26Mpa正常壓力0.26Mpa正常上模溫度193℃正常上模溫度193℃正常下模溫度241℃正常下模溫度241℃正常封口時(shí)間3S正常封口時(shí)間3S正常封口效果鋁帶極耳焦處過熔封口效果鋁帶極耳焦處過熔溶膠效果照片溶膠效果照片過熔頂封裝拉力測(cè)試試驗(yàn)方案：頂封壓力3.5～4kgf/cm2、上模溫度190℃、下模溫度250℃、封口時(shí)間3S、封頭寬度2MM封裝鋁塑膜后裁切小片8MM寬度±0.5MM、長(zhǎng)度20-25MM測(cè)試溶膠拉力。拉力>15N為合格頂封拉力（N）上海膜拉力深圳膜拉力454551464252514957355552464153374445檢查效果：試驗(yàn)鋁塑膜拉力>15N為合格側(cè)封裝拉力測(cè)試試驗(yàn)方案：側(cè)封壓力4.0～6.0kgf/cm2、上模溫度180℃、下模溫度180℃、封口時(shí)間3S、封頭寬度2MM封裝鋁塑膜后裁切小片8MM寬度±0.5MM、長(zhǎng)度20-25MM測(cè)試溶膠拉力。拉力>15N為合格側(cè)封拉力（N）上海膜拉力深圳膜拉力394040456841453954476636654368575651檢查效果：試驗(yàn)鋁塑膜拉力>15N為合格（對(duì)比我司生產(chǎn)鋁塑膜拉力測(cè)試對(duì)例如圖）HTA試驗(yàn)試驗(yàn)措施：取一定規(guī)格的鋁塑膜沖任意生產(chǎn)的型號(hào)規(guī)格的膜殼用極耳模擬封焊，注一定量的電解液編號(hào)，在45℃的老化房中放置半個(gè)小時(shí)后稱其重量，再將其旋轉(zhuǎn)在45℃的老化房中放置72個(gè)小時(shí)，再對(duì)應(yīng)先前編號(hào)稱其高溫烘烤后的重量，液矢量控制在≤0.1％。測(cè)試數(shù)據(jù)/g（上海鋁塑膜）測(cè)試數(shù)據(jù)/g（深圳鋁塑膜）序號(hào)前后損率%序號(hào)前后損率%17.0527.0510.0010.01%17.0427.051-0.009-0.13%27.1517.1450.0060.08%27.0117.02-0.009-0.13%37.2077.2030.0040.05%37.0737.0720.0010.01%47.2047.2020.0020.03%47.0627.060.0020.03%57.1987.1950.0030.04%57.0087.0050.0030.04%67.2067.2040.0020.03%67.0517.0450.0060.09%77.0267.0230.0030.04%77.0637.0610.0020.03%87.0537.0510.0020.03%87.0357.0310.0040.06%97.0277.0260.0010.01%97.077.0680.0020.03%107.0677.0660.0010.01%106.9976.9940.0030.04%最大值7.2077.2040.0060.08%最大值7.0737.0720.0010.01%最小值7.0267.0230.0010.01%最小值6.9976.9940.0030.04%平均值7.1197.1170.00250.03%平均值7.04127.04070.00050.01%鑒定原則：率≤0.1%OK鑒定原則：率≤0.1%OK45℃72h抽真空烘烤試驗(yàn)圖片尼龍層耐電解液試驗(yàn)試驗(yàn)措施：在電芯表面滴加1-2滴電解液，放置45℃48h觀測(cè)表面尼龍層變化狀況；鑒定原則：局部電解污染不能起泡分層脫落。放制前放制后試驗(yàn)成果：局部電解污染不起泡、不分層、不脫落。測(cè)試合格。十、45℃30天電池觀測(cè)試驗(yàn)措施：45℃30天電池觀測(cè)：載體，每隔3天觀測(cè)一次，電池?zé)o漏液，無氣脹，無起火等異?，F(xiàn)象；序號(hào)觀測(cè)日期鋁塑膜狀況12345678910開始圖片結(jié)束圖片供應(yīng)商XX鋁塑膜型號(hào)規(guī)格400*0.113mm使用電芯80500/D0600測(cè)試條件正常生產(chǎn)流程檢查項(xiàng)目測(cè)試原則檢查成果1外觀無針孔、異物、粘連、涂層不均勻、氣泡、皺紋、臟物等缺陷合格2測(cè)試厚度0.113um合格3冷沖壓成型性是沖80系列不分層、破裂、針孔漏光合格4尼龍層耐電解液浸泡試驗(yàn)溫度45℃用電解液浸泡48小時(shí)，PP不分層鋁層不導(dǎo)通；尼龍層以鋁層分層后鋁層不能變色。合格5熔膠試驗(yàn)撕開封接處，鋁塑膜兩邊粘有均勻CPP并帶乳白色封印良好合格6HTA試驗(yàn)取一定規(guī)鋁取一45℃12h抽真空-0.08mpa試驗(yàn)，外觀：表面尼龍層不脫層，封接處不裂開，并由失重率判斷封接效果：鑒定原則：率≤0.1%7尼龍層耐電解液試驗(yàn)在電芯表面滴加1-2滴電解液，放置45℃48h觀測(cè)表面尼龍層無大面積脫層合格8電池45℃30天觀測(cè)45℃30天電池觀測(cè)：載體，每隔3天觀測(cè)一次，電池?zé)o漏液，無氣脹，無起火等異?，F(xiàn)象9高溫高濕電池完全充電后，放入70±2℃、相對(duì)濕度為90%~95%的恒溫恒濕箱中擱置7天試驗(yàn)效果評(píng)估結(jié)論成型80系列單封邊深、淺槽沖殼深度4.0/3.0±0.1mm不分層、破裂、針孔漏光13系列單封邊深、淺槽沖殼深度5.8/5.8±0.1mm不分層、破裂、針孔漏