《高速公路瀝青路面施工技術(shù)規(guī)范》

DB32/T—2022

目次

前言.................................................................................VI

1范圍...............................................................................1

2規(guī)范性引用文件.....................................................................1

3術(shù)語和定義.........................................................................2

4符號和縮略語.......................................................................5

5總體要求...........................................................................6

6基層、底基層.......................................................................6

6.1一般規(guī)定.......................................................................6

6.2抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層.............................................6

6.3密級配瀝青碎石混合料基層......................................................12

6.4級配碎石底基層................................................................13

6.5質(zhì)量管理和檢查驗收............................................................15

7下封層、粘層......................................................................18

7.1下封層........................................................................18

7.2粘層..........................................................................19

7.3質(zhì)量管理和檢查驗收............................................................20

8水泥混凝土橋面防水粘結(jié)層..........................................................20

8.1一般規(guī)定......................................................................20

8.2材料要求......................................................................21

8.3施工準(zhǔn)備......................................................................21

8.4施工..........................................................................21

8.5質(zhì)量管理和檢查驗收............................................................22

9面層..............................................................................22

9.1一般規(guī)定......................................................................22

9.2材料要求......................................................................23

9.3瀝青混合料技術(shù)要求............................................................27

9.4瀝青混合料配合比設(shè)計..........................................................29

9.5下承層的檢查與處理............................................................31

9.6機械與試驗儀器................................................................32

9.7首件工程......................................................................32

9.8施工..........................................................................33

9.9其他瀝青混合料................................................................36

9.10質(zhì)量管理和檢查驗收...........................................................40

10改擴建工程.......................................................................42

10.1一般規(guī)定.....................................................................42

10.2材料要求.....................................................................42

I

DB32/T—2022

10.3舊路面的處理..................................................................42

10.4新舊路面鋪筑及拼接............................................................43

11施工信息自動采集與預(yù)警............................................................46

11.1一般規(guī)定......................................................................46

11.2數(shù)據(jù)采集與傳輸................................................................46

11.3數(shù)據(jù)分析與預(yù)警處理............................................................48

附錄A（規(guī)范性）施工機械............................................................49

附錄B（規(guī)范性）質(zhì)量檢測儀器........................................................52

附錄C（資料性）ATB-25瀝青碎石混合料目標(biāo)配合比設(shè)計實例..............................55

附錄D（規(guī)范性）不粘輪試驗規(guī)程......................................................59

附錄E（規(guī)范性）AC-S瀝青混合料要求..................................................61

附錄F（規(guī)范性）公路瀝青60℃旋轉(zhuǎn)粘度試驗規(guī)程........................................62

附錄G（規(guī)范性）多應(yīng)力蠕變恢復(fù)（MSCR）試驗方法檢測規(guī)程...............................64

附錄H（資料性）玄武巖高溫抗剝落性能試驗規(guī)程.........................................68

附錄I（規(guī)范性）粗集料高溫壓碎值試驗規(guī)程.............................................70

附錄J（規(guī)范性）液體材料滲透性試驗規(guī)程..............................................72

附錄K（資料性）SMA-13S瀝青混合料目標(biāo)配合比設(shè)計實例.................................74

附錄L（資料性）Superpave20瀝青混合料目標(biāo)配合比設(shè)計實例.............................78

附錄M（規(guī)范性）地推式直剪試驗檢測規(guī)程..............................................84

參考文獻..............................................................................85

圖C.1混合料密度及體積指標(biāo)與油石比關(guān)系曲線..........................................57

圖D.1粘輪測試儀示意圖.............................................................59

圖F.1布洛克菲爾德粘度計示意圖......................................................62

圖G.1動態(tài)剪切流變儀基本原理示意圖..................................................64

圖K.1級配曲線圖....................................................................75

圖L.1設(shè)計級配曲線..................................................................80

圖M.1地推式直剪試驗裝置示意圖......................................................84

表1水泥質(zhì)量要求.....................................................................7

表2集料備料規(guī)格.....................................................................7

表3粗集料技術(shù)要求...................................................................7

表4細集料技術(shù)要求...................................................................7

表5抗裂嵌擠型（低劑量）水泥穩(wěn)定碎石混合料級配范圍....................................9

表6密級配瀝青碎石混合料級配范圍....................................................12

表7密級配瀝青碎石混合料大馬歇爾試驗設(shè)計要求.........................................12

表8級配碎石底基層用集料質(zhì)量技術(shù)要求................................................13

表9級配碎石級配組成范圍............................................................13

II

DB32/T—2022

表10水泥、集料的質(zhì)量標(biāo)準(zhǔn)...........................................................15

表11抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層質(zhì)量控制標(biāo)準(zhǔn).................................16

表12級配碎石底基層施工過程中質(zhì)量檢查標(biāo)準(zhǔn)...........................................17

表13SBS改性乳化瀝青技術(shù)要求.......................................................18

表14集料級配范圍...................................................................19

表15不粘輪乳化瀝青技術(shù)要求.........................................................20

表16下封層質(zhì)量檢查項目及質(zhì)量標(biāo)準(zhǔn)...................................................20

表17水泥混凝土橋面防水粘結(jié)層的檢驗標(biāo)準(zhǔn).............................................22

表1870號道路石油瀝青技術(shù)要求......................................................23

表19SBS改性瀝青技術(shù)要求...........................................................23

表20面層用粗集料技術(shù)要求...........................................................24

表21粗集料供料品種控制篩孔尺寸.....................................................25

表22面層用細集料規(guī)格...............................................................25

表23面層用細集料技術(shù)要求...........................................................25

表24面層用礦粉的技術(shù)要求...........................................................26

表25抗剝落劑技術(shù)要求...............................................................26

表26封水劑技術(shù)要求.................................................................27

表27SMA-13S瀝青混合料馬歇爾試驗設(shè)計技術(shù)要求.......................................27

表28SMA-13S瀝青混合料配合比檢驗技術(shù)要求...........................................27

表29Superpave20瀝青混合料配合比設(shè)計及驗證試驗技術(shù)要求.............................28

表30Superpave25瀝青混合料配合比設(shè)計及驗證試驗技術(shù)要求.............................28

表31SMA-13S瀝青混合料級配范圍.....................................................29

表32Superpave瀝青混合料級配控制點和限制區(qū)界限.....................................29

表33瀝青混合料施工溫度.............................................................33

表34Superpave混合料碾壓速度.......................................................34

表35SMA-13S混合料碾壓速度.........................................................35

表36高模量劑質(zhì)量技術(shù)要求...........................................................36

表37HMM級配范圍...................................................................36

表38HMM配合比設(shè)計檢驗技術(shù)要求.....................................................36

表39HMM的施工溫度.................................................................37

表40建議施工碾壓方案...............................................................38

表41巖瀝青質(zhì)量技術(shù)要求.............................................................38

表42RAC-20級配范圍................................................................38

表43RAC-20馬歇爾試驗設(shè)計及檢驗要求................................................38

表44RAC-20的施工溫度..............................................................40

表45建議施工碾壓方案...............................................................40

表46瀝青路面各面層施工階段的質(zhì)量檢查標(biāo)準(zhǔn)...........................................40

表47界面劑技術(shù)要求.................................................................44

表48基層、底基層拼接縫施工質(zhì)量控制要求.............................................44

表49面層拼接縫施工質(zhì)量控制要求.....................................................45

表50改性瀝青生產(chǎn)指標(biāo)及采集頻率.....................................................46

表51瀝青運輸指標(biāo)及采集頻率.........................................................46

表52瀝青試驗檢測指標(biāo)及采集頻率.....................................................46

III

DB32/T—2022

表53瀝青混合料拌和生產(chǎn)指標(biāo)及采集頻率................................................47

表54瀝青混合料運輸指標(biāo)及采集頻率...................................................47

表55瀝青混合料攤鋪指標(biāo)及采集頻率...................................................47

表56瀝青混合料壓實指標(biāo)及采集頻率...................................................48

表A.1底基層、基層施工機械設(shè)備配置..................................................49

表A.2SMA-13S上面層施工機械設(shè)備配置.................................................49

表A.3Superpave面層施工機械設(shè)備配置.................................................50

表A.4HMM面層施工機械設(shè)備配置.......................................................50

表A.5RAC面層施工機械設(shè)備配置.......................................................50

表A.6下封層施工機械設(shè)備配置........................................................51

表A.7橋面防水粘結(jié)層施工機械設(shè)備配置................................................51

表B.1基層、底基層質(zhì)量檢測儀器配置..................................................52

表B.2瀝青面層質(zhì)量檢測儀器配置......................................................52

表B.3下封層質(zhì)量檢測儀器配置........................................................53

表B.4橋面防水粘結(jié)層質(zhì)量檢測儀器配置................................................54

表C.1各種集料篩分結(jié)果.............................................................55

表C.2各級配各種集料組成...........................................................55

表C.3混合料級配表.................................................................55

表C.4各級配的大馬歇爾試驗結(jié)果.....................................................55

表C.5各級配混合料SSC試驗結(jié)果.....................................................56

表C.6設(shè)計級配不同油石比時大馬歇爾試驗結(jié)果..........................................57

表C.7設(shè)計級配各項指標(biāo).............................................................57

表C.8水穩(wěn)定性試驗結(jié)果.............................................................58

表C.9動穩(wěn)定度試驗結(jié)果.............................................................58

表C.10無側(cè)限抗壓強度試驗結(jié)果（20℃）..............................................58

表E.1AC-20S、AC-25S瀝青混合料級配組成.............................................61

表G.1控制和數(shù)據(jù)采集系統(tǒng)精度要求...................................................64

表H.1瀝青混合料試樣數(shù)量...........................................................68

表H.2瀝青混合料試樣數(shù)量...........................................................68

表K.1各種集料的篩分結(jié)果...........................................................74

表K.2集料密度試驗結(jié)果.............................................................74

表K.3SMA-13S瀝青混合料三種級配的設(shè)計組成結(jié)果......................................74

表K.4VCADRC測試結(jié)果.................................................................75

表K.5初試級配的體積分析...........................................................75

表K.6馬歇爾試驗結(jié)果...............................................................75

表K.7析漏試驗結(jié)果.................................................................76

表K.8飛散試驗結(jié)果.................................................................76

表K.9浸水馬歇爾試驗結(jié)果...........................................................76

表K.10車轍試驗動穩(wěn)定度............................................................76

表K.11小梁彎曲試驗結(jié)果............................................................77

表K.12級配及最佳油石比............................................................77

表L.1集料相對密度試驗結(jié)果表.......................................................78

表L.2集料篩分結(jié)果表...............................................................78

IV

DB32/T—2022

表L.3級配組成表...................................................................78

表L.4三種試驗級配旋轉(zhuǎn)壓實試驗結(jié)果匯總表...........................................79

表L.5三種級配估算瀝青用量試驗結(jié)果評價表...........................................79

表L.6設(shè)計級配四種瀝青用量試驗結(jié)果匯總表...........................................80

表L.7四種瀝青用量瀝青混合料體積性質(zhì)...............................................81

表L.8設(shè)計瀝青用量驗證試驗結(jié)果表...................................................81

表L.9瀝青混合料體積性質(zhì)表.........................................................81

表L.10瀝青混合料馬歇爾試驗結(jié)果....................................................82

表L.11車轍試驗動穩(wěn)定度試驗結(jié)果....................................................82

表L.12浸水馬歇爾穩(wěn)定度試驗結(jié)果....................................................82

表L.13凍融劈裂試驗結(jié)果............................................................82

表L.14小梁彎曲試驗結(jié)果............................................................83

表L.15級配及設(shè)計油石比............................................................83

V

DB32/T—2022

前言

本文件按照GB/T1.1—2020《標(biāo)準(zhǔn)化工作導(dǎo)則第1部分：標(biāo)準(zhǔn)化文件的結(jié)構(gòu)和起草規(guī)則》的規(guī)定

起草。

本文件代替DB32/T1087—2008《江蘇省高速公路瀝青路面施工技術(shù)規(guī)范》，與DB32/T1087—2008

相比除了編輯性修改外，主要技術(shù)變化如下：

a)更改了部分術(shù)語（見第3章，2008年版的第3章）；

b)更改了部分符號（見第4章，2008年版的第4章）；

c)更改了底基層、基層（見第6章，2008年版的第6章、第7章）；

d)刪除了石灰粉煤灰穩(wěn)定土底基層（見2008年版的6.2）；

e)更改了抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層（見6.2，2008年版的6.4、7.2）；

f)刪除了石灰粉煤灰碎石基層、底基層（見2008年版的6.4、7.3）；

g)刪除了路面透層（見2008年版的8.1）；

h)更改了路面下封層、粘層技術(shù)要求（見7.1、7.2,2008年版的8.2、8.3）；

i)更改了水泥混凝土橋面防水粘結(jié)層（見第8章，2008年版的第9章）

j)更改了面層材料、瀝青混合料技術(shù)要求（見9.2、9.3，2008年版的10.2、10.3）；

k)刪除了面層中AC/AK瀝青混合料相關(guān)要求（見2008年版的第10章）；

l)增加了高模量瀝青混合料、巖瀝青混合料技術(shù)要求（見9.9）；

m)更改了新舊路面基層、面層拼接方法（見10.3、10.4，2008年版的11.3、11.4）；

n)增加了施工信息自動采集與預(yù)警（見第11章）；

o)更改了“施工機械”、“質(zhì)量檢測儀器”、“熱拌瀝青混合料馬歇爾試驗設(shè)計方法”、“瀝

青混合料Superpave配合比設(shè)計方法”、“ATB瀝青碎石混合料的配合比設(shè)計”（見附錄A、

附錄B、附錄K、附錄L、附錄C，2008年版的附錄A、附錄B、附錄C、附錄D）；

p)刪除了“施工質(zhì)量動態(tài)管理方法”（見2008年版附錄E）；

q)增加了“不粘輪試驗規(guī)程”、“AC-S瀝青混合料要求”、“公路瀝青60℃旋轉(zhuǎn)粘度試驗規(guī)程”、

“多應(yīng)力蠕變恢復(fù)（MSCR）試驗方法檢測規(guī)程”、“玄武巖高溫抗剝落性能試驗規(guī)程”、“粗

集料高溫壓碎值試驗規(guī)程”、“液體材料滲透性試驗規(guī)程”、“地推式直剪試驗檢測規(guī)程”

（見附錄D、附錄E、附錄F、附錄G、附錄H、附錄I、附錄J、附錄M）。

請注意本文件的某些內(nèi)容可能涉及專利。本文件的發(fā)布機構(gòu)不承擔(dān)識別專利的責(zé)任。

本文件由江蘇省交通運輸廳提出并歸口。

本文件起草單位：江蘇省交通工程建設(shè)局、江蘇中路工程技術(shù)研究院有限公司、中路交科科技股份

有限公司。

本文件主要起草人：蔣振雄、劉世同、潘衛(wèi)育、張志祥、杜騁、金光來、劉朝暉、邵學(xué)富、陸宇、

李一鶴、楊光昊、張孝勝、王祥波、蔡文龍、臧國帥、劉海婷、曹陽、張志超、余雪娟、吳德磊、王兆

鑫、陳兆南、馬仕亮、王罡。

本文件及其所代替文件的歷次版本發(fā)布情況為：

——2008年首次發(fā)布為DB32/T1087—2008；

——本次為第一次修訂。

VI

DB32/T—2022

高速公路瀝青路面施工技術(shù)規(guī)范

1范圍

本文件規(guī)定了高速公路瀝青路面底基層、基層、下封層、粘層、水泥混凝土橋面防水粘結(jié)層、面層

等施工技術(shù)要求，改擴建工程、施工信息自動采集與預(yù)警等要求。

本文件適用于高速公路新建、改擴建瀝青路面等工程，其他等級公路可參照執(zhí)行。

2規(guī)范性引用文件

下列文件中的內(nèi)容通過文中的規(guī)范性引用而構(gòu)成本文件必不可少的條款。其中，注日期的引用文件，

僅該日期對應(yīng)的版本適用于本文件；不注日期的引用文件，其最新版本（包括所有的修改單）適用于本

文件。

GB/T1346水泥標(biāo)準(zhǔn)稠度用水量、凝結(jié)時間、安定性檢驗方法

GB/T3682.1塑料熱塑性塑料熔體質(zhì)量流動速率（MFR）和熔體體積流動速率（MVR）的測定第1

部分：標(biāo)準(zhǔn)方法

GB/T5210色漆和清漆拉開法附著力試驗

GB/T17671水泥膠砂強度檢驗方法(ISO法)

GB/T19466.3塑料差示掃描量熱法(DSC)第3部分：熔融和結(jié)晶溫度及熱焓的測定

JCT975道橋用防水涂料

JGJ63混凝土用水標(biāo)準(zhǔn)

JT/T533瀝青路面用纖維

JT/T798路用廢胎膠粉橡膠瀝青

JTG3430公路土工試驗規(guī)程

JTG3450公路路基路面現(xiàn)場測試規(guī)程

JTG5142公路瀝青路面養(yǎng)護技術(shù)規(guī)范

JTG5421公路瀝青路面養(yǎng)護設(shè)計規(guī)范

JTG/T5521公路瀝青路面再生技術(shù)規(guī)范

JTGD50公路瀝青路面設(shè)計規(guī)范

JTGE20公路工程瀝青及瀝青混合料試驗規(guī)程

JTGE30公路工程水泥及水泥混凝土試驗規(guī)程

JTGE41公路工程巖石試驗規(guī)程

JTGE42公路工程集料試驗規(guī)程

JTGE51公路工程無機結(jié)合料穩(wěn)定材料試驗規(guī)程

JTG/TF20公路路面基層施工技術(shù)細則

JTGF40公路瀝青路面施工技術(shù)規(guī)范

JTGF80/1公路工程質(zhì)量檢驗評定標(biāo)準(zhǔn)第一冊土建工程

DB32/T2285水泥混凝土橋面水性環(huán)氧瀝青防水粘結(jié)層施工技術(shù)規(guī)范

DB32/T3821公路養(yǎng)護工程排水瀝青路面技術(shù)規(guī)范

DB32/TXXXX瀝青紅外光譜指紋識別與SBS摻量試驗檢測規(guī)程

1

DB32/T—2022

3術(shù)語和定義

下列術(shù)語和定義適用于本文件。

3.1

基層base

直接位于瀝青路面面層下的主要承重層。

[來源：JTG/TF20—2015，2.0.1，有修改]

3.2

底基層subbase

在瀝青路面基層下鋪裝的次要承重層。

[來源：JTG/TF20—2015，2.0.2，有修改]

3.3

抗裂嵌擠型水泥穩(wěn)定碎石cementstabilizedmaterialwithcrackresistanceandinterlock

characteristics

通過混合料合成級配的控制，形成骨架嵌擠結(jié)構(gòu)的水泥穩(wěn)定碎石混合料。

[來源：DB32/T3311—2017，3.3]

3.4

抗裂嵌擠型低劑量水泥穩(wěn)定碎石low-dosecementstabilizedmaterialwithcrackresistance

andinterlockcharacteristics

采用較低劑量（一般小于3%）的水泥，通過混合料合成級配的控制，形成骨架嵌擠結(jié)構(gòu)的水泥穩(wěn)

定碎石混合料。

3.5

級配碎石gradedcrushedstone

各檔粒徑的碎石和石屑按一定比例混合，級配滿足一定要求且塑性指數(shù)和承載比均符合規(guī)定要求的

混合料。

[來源：JTG/TF20—2015，2.0.7]

3.6

松鋪系數(shù)coefficientofloosepavingmaterial

材料的松鋪厚度與達到規(guī)定壓實度的壓實厚度之比值。

[來源：JTG/TF20—2015，2.0.10]

3.7

集料aggregate

在混合料中起骨架和填充作用的粒料，包括碎石、石屑、砂等。

[來源：JTGE42—2005，2.1.1]

3.8

填料filler

在瀝青混合料中起填充作用的粒徑小于0.075mm的礦物質(zhì)粉末。通常是石灰石等堿性石料加工磨細

得到的礦粉，水泥、消石灰、粉煤灰等礦物質(zhì)有時也可作為填料使用。

[來源：JTGE42—2005，2.1.9]

3.9

聚合物纖維polymerfiber

2

DB32/T—2022

以合成高分子聚合物為原料制成的化學(xué)纖維。

[來源：JT/T533—2020，3.3]

3.10

集料最大粒徑maximumsizeofaggregate

指集料的100%都要求通過的最小的標(biāo)準(zhǔn)篩篩孔尺寸。

[來源：JTGE42—2005，2.1.27]

3.11

集料的公稱最大粒徑nominalmaximumsizeofaggregate

指集料有少量不通過（一般容許篩余不超過10%）的最小標(biāo)準(zhǔn)篩篩孔尺寸。通常比集料最大粒徑小

一個粒級。

[來源：JTGE42—2005，2.1.28]

3.12

瀝青結(jié)合料Asphaltbinder，Asphaltcement

在瀝青混合料中起膠結(jié)作用的瀝青類材料（含添加的外摻劑、改性劑等）的總稱。

[來源：JTGF40—2004，2.1.1]

3.13

乳化瀝青emulsifiedbitumen（英），asphaltemulsion，emulsifiedasphalt（美）

石油瀝青（或煤瀝青）與水在乳化劑、穩(wěn)定劑的作用下經(jīng)乳化加工制得的均勻的瀝青產(chǎn)品，也稱瀝

青乳液。

[來源：JTGF40—2004，2.1.2]

3.14

改性瀝青modifiedbitumen（英），modifiedasphalt（美）

摻加橡膠、樹脂、高分子聚合物、天然瀝青、磨細的橡膠粉或者其他材料等外摻劑（改性劑）制成

的瀝青結(jié)合料，從而使瀝青或瀝青混合料的性能得以改善。

[來源：JTGF40—2004，2.1.4]

3.15

改性乳化瀝青modifiedemulsifiedbitumen（英），modifiedasphaltemulsion（美）

在制作乳化瀝青的過程中同時加入聚合物膠乳，或?qū)⒕酆衔锬z乳與乳化瀝青成品混合，或?qū)酆衔?/p>

改性瀝青進行乳化加工得到的乳化瀝青產(chǎn)品。

[來源：JTGF40—2004，2.1.5]

3.16

不粘輪乳化瀝青non-stickwheelemulsifiedasphalt

由特種瀝青與乳化劑、改性劑、穩(wěn)定劑等制備而成的，具有較強粘結(jié)性能及抵抗施工機械輪胎、履

帶等損傷性能的粘層材料。

3.17

粘（黏）層tackcoat

路面結(jié)構(gòu)中起粘結(jié)作用的功能層。

[來源：JTGD50—2017，2.1.9]

3.18

封層sealcoat

路面結(jié)構(gòu)中用以阻止水下滲的功能層。

3

DB32/T—2022

[來源：JTGD50—2017，2.1.8]

3.19

橋面防水粘結(jié)層bridgedeckwaterproofbondinglayer

設(shè)在橋面水泥混凝土鋪裝層與瀝青鋪裝層之間，起防水和粘結(jié)作用的薄層。

3.20

傅立葉變換紅外光譜fouriertransforminfraredspectroscopy

FTIR

一種通過獲得固體,液體或氣體的紅外線吸收光譜和放射光譜。

注：可用于評價瀝青相似度與測定改性瀝青中SBS含量。

3.21

瀝青旋轉(zhuǎn)粘度asphaltrotationalviscosity

采用布洛克菲爾德粘度計測定瀝青試樣流動時形成的抵抗力或內(nèi)部阻力度量。

3.22

多應(yīng)力蠕變恢復(fù)multiplestresscreeprecovery

MSCR

瀝青試樣經(jīng)過不同應(yīng)力水平下力的一定周期作用后，瀝青的應(yīng)變恢復(fù)率。

3.23

封水劑sealingagent

用于封堵瀝青路面表面空隙及微裂縫，以提高瀝青路面密水性的材料。

3.24

瀝青混合料bituminousmixtures（英），asphaltmixtures（美）

由礦料與瀝青結(jié)合料拌和而成的混合料的總稱。按材料組成及結(jié)構(gòu)分為連續(xù)級配、間斷級配混合料。

按礦料級配組成及空隙率大小分為密級配、半開級配、開級配混合料。按公稱最大粒徑的大小可分為特

粗式（公稱最大粒徑等于或大于31.5mm）、粗粒式（公稱最大粒徑26.5mm）、中粒式（公稱最大粒徑16mm

或19mm）、細粒式（公稱最大粒徑9.5mm或13.2mm）、砂粒式（公稱最大粒徑小于9.5mm）瀝青混合料。

[來源：JTGF40—2004，2.1.12]

3.25

瀝青瑪蹄脂碎石混合料stonemasticasphalt（英），stonematrixasphalt（美）

由瀝青膠結(jié)料與少量的纖維穩(wěn)定劑、細集料以及較多量的填料（礦粉）組成的瀝青瑪蹄脂，填充于

間斷級配的粗集料骨架間隙，組成一體形成的瀝青混合料，簡稱SMA。

[來源：JTGF40—2004，2.1.18]

3.26

密級配瀝青碎石混合料（瀝青穩(wěn)定碎石基層）dense-gradedasphaltgravelmixture（asphalt

treatedbase）

ATB

由礦料和瀝青組成的有一定級配要求的密級配瀝青處治碎石混合料。

3.27

高模量瀝青混合料highmodulusmixture

HMM

采用硬質(zhì)瀝青、硬質(zhì)瀝青顆?；蚋吣Ａ縿┑茸鳛樘砑觿┡c瀝青、集料拌和成型，具有設(shè)計空隙率小、

高模量、抗車轍、密水等特點，用于路面抗車轍層的混合料。

4

DB32/T—2022

3.28

巖瀝青混合料rockasphaltmixture

RAC

采用天然巖瀝青作為添加劑與瀝青、集料拌和成型，具有抗車轍性能好、強度高等特點，用于路面

抗車轍層的混合料。

4符號和縮略語

下列符號適用于本文件。

C：集料的瀝青吸收系數(shù)

Pa：瀝青混合料的油石比

Pb：瀝青混合料中的瀝青用量

Pbe：瀝青混合料中的有效瀝青用量

γb：瀝青的相對密度

γsa：瀝青混合料中合成礦料的表觀相對密度

γsb：瀝青混合料中合成礦料的毛體積相對密度

γse：瀝青混合料中合成礦料的有效相對密度

γt：瀝青混合料的最大理論相對密度

下列縮略語適用于本文件。

AC-S：適用于江蘇省高速公路的密級配瀝青混合料

ATB：密級配瀝青碎石混合料

CBR：加州承載比

DP：瀝青混合料的粉膠比（0.075mm通過率與有效瀝青含量的比值）

DS：動穩(wěn)定度

FL：馬歇爾試驗的流值

FTIR：傅立葉變換紅外光譜

HMM：高模量瀝青混合料

MS：馬歇爾穩(wěn)定度

MSCR：多應(yīng)力蠕變恢復(fù)

OAC：最佳瀝青用量

OGFC：開級配抗滑表層

PG：美國瀝青膠結(jié)料路用性能分級規(guī)范

PI：瀝青膠結(jié)料針入度指數(shù)

RAC：巖瀝青混合料

RTFOT/TFOT：旋轉(zhuǎn)薄膜加熱（薄膜加熱）試驗

SBS：苯乙烯—丁二烯—苯乙烯嵌段共聚物

SGC：旋轉(zhuǎn)壓實試驗機

SMA-S：適用于江蘇省高速公路的瀝青瑪蹄脂碎石混合料

SuperpaveTM：美國公路戰(zhàn)略研究計劃

TSR：凍融劈裂試驗強度比

5

DB32/T—2022

VCA：粗集料骨架間隙率

VCADRC：搗實狀態(tài)下的粗集料松裝間隙率

VCAmix：壓實瀝青混合料的粗集料骨架間隙率

VFA：壓實瀝青混合料中的瀝青飽和度

VMA：壓實瀝青混合料的礦料間隙率

VV：壓實瀝青混合料的空隙率

5總體要求

5.1應(yīng)結(jié)合本地實際選擇高速公路瀝青路面合適的結(jié)構(gòu)和材料，鼓勵采用經(jīng)試驗和實踐檢驗的新技術(shù)、

新材料、新設(shè)備、新工藝。

5.2應(yīng)執(zhí)行國家環(huán)境和生態(tài)保護、安全生產(chǎn)的相關(guān)規(guī)定。

5.3應(yīng)編制施工組織設(shè)計方案。

5.4試驗檢測的試驗室和試驗人員應(yīng)取得相應(yīng)的資質(zhì)，儀器設(shè)備應(yīng)檢定合格。

6基層、底基層

6.1一般規(guī)定

6.1.1高速公路瀝青路面基層宜采用抗裂嵌擠型水泥穩(wěn)定碎石。

6.1.2根據(jù)工程實際情況和各類基層的適用條件，可選擇其他的基層類型，如密級配瀝青碎石基層、

開級配瀝青碎石基層等。

6.1.3可采用雙層連鋪或整層一次性全厚度攤鋪施工。

注1：雙層連鋪是指在施工完下基層適當(dāng)長度后，即刻施工上基層的一種施工方式。

注2：整層一次性全厚度攤鋪是指采用大功率攤鋪機一次性攤鋪兩層基層，并碾壓成型至基層設(shè)計厚度的一種施工

方式。

6.1.4高速公路瀝青路面底基層宜采用抗裂嵌擠型低劑量水泥穩(wěn)定碎石，可采用廠拌水泥再生碎石、

級配碎石等。

6.1.5廠拌水泥再生碎石底基層，應(yīng)按照J(rèn)TG/T5521的有關(guān)規(guī)定執(zhí)行。

6.1.6應(yīng)控制基層、底基層厚度和高程，其橫坡應(yīng)與面層一致?；鶎?、底基層表面高出設(shè)計標(biāo)高部分

應(yīng)銑刨處理；局部標(biāo)高低于驗收標(biāo)準(zhǔn)，應(yīng)銑刨重鋪。

6.2抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層

6.2.1一般要求

6.2.1.1高速公路瀝青路面基層、底基層采用抗裂嵌擠型水泥穩(wěn)定碎石結(jié)構(gòu)時，應(yīng)采用集中廠拌工藝，

單層壓實厚度宜為18cm～20cm。

6.2.1.2抗裂嵌擠型水泥穩(wěn)定碎石混合料采用干質(zhì)量配合比計算，以集料100，水泥劑量外加的外比

表示。

6.2.1.3宜在氣溫較高的季節(jié)組織施工。施工期的日最低氣溫應(yīng)在5℃以上，在有冰凍的地區(qū)，應(yīng)在

第一次重冰凍到來的15d～30d之前完成施工。

注：重冰凍的標(biāo)準(zhǔn)一般指氣溫達到-3℃～-5℃。

6

DB32/T—2022

6.2.1.4應(yīng)盡可能縮短從加水拌和到碾壓終了的延遲時間，延遲時間不應(yīng)超過水泥的初凝時間。

6.2.1.5雨季施工時，應(yīng)避免抗裂嵌擠型水泥穩(wěn)定碎石混合料遭雨淋。

6.2.1.6應(yīng)采取有效措施，防止抗裂嵌擠型水泥穩(wěn)定碎石基層、底基層在施工中出現(xiàn)離析和開裂現(xiàn)象，

對已經(jīng)出現(xiàn)的離析和開裂應(yīng)進行處理。

6.2.2材料要求

6.2.2.1水泥

6.2.2.1.1普通硅酸鹽水泥、礦渣硅酸鹽水泥、火山灰質(zhì)硅酸鹽水泥都可用于拌和抗裂嵌擠型水泥穩(wěn)

定碎石混合料，宜采用強度等級不低于42.5級的緩凝水泥，水泥初凝、終凝時間應(yīng)符合表1規(guī)定，其

他指標(biāo)應(yīng)符合JTGE30與GB/T1346的規(guī)定。

6.2.2.1.2采用散裝水泥，安定性應(yīng)檢測合格后入罐使用，水泥溫度應(yīng)不高于50℃。

表1水泥質(zhì)量要求

項次檢測項目技術(shù)要求試驗方法

1初凝時間＞3h

GB/T1346

2終凝時間＞6h且＜10h

6.2.2.2集料

6.2.2.2.1集料的最大粒徑為31.5mm，4.75mm及以上為粗集料、4.75mm以下為細集料。宜按四種及

以上規(guī)格備料，備料規(guī)格應(yīng)符合表2的規(guī)定。

表2集料備料規(guī)格

項次粒徑規(guī)格/mm

1四檔集料13.2～31.54.75～13.22.36～4.750～2.36—

2五檔集料19.0～31.59.5～19.04.75～9.52.36～4.750～2.36

6.2.2.2.2粗集料的技術(shù)要求應(yīng)符合表3的規(guī)定，細集料的技術(shù)要求應(yīng)符合表4的規(guī)定；粗、細集料

規(guī)格應(yīng)符合JTG/TF20相關(guān)規(guī)定。

表3粗集料技術(shù)要求

技術(shù)要求

項次檢驗項目試驗方法

基層底基層

1壓碎值≤26%≤30%JTGE42，T0316

2針片狀顆粒含量≤15%JTGE42，T0312

3軟石含量≤5%JTGE42，T0320

4小于0.075mm顆粒含量≤2%JTGE42，T0310

表4細集料技術(shù)要求

項次檢驗項目技術(shù)要求試驗方法

1液限＜28%JTG3430，T0118

2塑性指數(shù)＜9JTG3430，T0118

7

DB32/T—2022

表4（續(xù)）

項次檢驗項目技術(shù)要求試驗方法

3硫酸鹽含量≤0.25%JTGE42，T0341

4有機質(zhì)含量＜2%JTGE42，T0336

5小于1.18mm顆粒含量（2.36mm～4.75mm規(guī)格）≤5%JTGE42，T0333

6小于0.075mm顆粒含量（0～2.36mm規(guī)格）≤15%JTGE42，T0333

7顆粒分析符合JTG/TF20細集料規(guī)格要求JTGE42，T0327

6.2.2.3水

飲用水可直接作為拌和與養(yǎng)生用水。非飲用水技術(shù)要求應(yīng)符合JGJ63的規(guī)定。

6.2.3機械與試驗儀器

應(yīng)配備齊全的施工機械和試驗儀器，開工前應(yīng)進行保養(yǎng)和試機工作，主要施工機械和試驗儀器配備

應(yīng)符合附錄A和附錄B要求。

6.2.4配合比設(shè)計

6.2.4.1一般規(guī)定

6.2.4.1.1抗裂嵌擠型水泥穩(wěn)定碎石混合料配合比設(shè)計，分為目標(biāo)配合比設(shè)計與生產(chǎn)配合比設(shè)計。

6.2.4.1.2根據(jù)規(guī)定的材料指標(biāo)要求，通過試驗選取合適的集料和水泥；確定合理的集料配合比例、

最佳水泥劑量、混合料的最佳含水量和相應(yīng)的最大干密度。

6.2.4.1.3為減少基層裂縫，應(yīng)做到三個限制：在滿足設(shè)計強度的基礎(chǔ)上限制水泥用量；同時限制細

集料用量；根據(jù)施工時氣候條件限制含水量。施工中水泥劑量宜不大于4.2%，合成集料級配中0.075mm

以下顆粒含量宜不大于