1、die life of cold stamping die and mprovementsoverview of stamping die stamping die - stamping in the cold, the material (metal or non-metallic) processing into parts (or half) of a special technical equipment, called cold stamping die (commonly known as die). press - is at room temperature, using th

2、e die installed in the press to put pressure on the material to produce a separation or plastic deformation, and thus to obtain the necessary parts of a pressure processing method. stamping die in the form of many, the general categories according to the following main features: 1. according to the

3、technical nature of (1) die along the closed or open contour the material are derived from mold. if blanking die, punch die, cut off the mold, cut mode, cutting mode, split mode, etc. (2) bending mode to blank or blank sheet along a straight line (curved line) to bend, deform, and thus obtain a cert

4、ain angle and shape of the workpiece in the mold. (3) the drawing die is made of the blank sheet opening hollow, or hollow pieces of further changes to the shape and size of the mold. (4) die rough or semi-finished workpiece is convex according to plan, direct copy the shape of the die shape, the ma

5、terial itself, generate only local plastic deformation of the mold. such as the bulging mode, reducing the die, expansion die, forming die rolling, flanging mold, plastic mold. 2. according to the degree classification process combination (1) single process model in a press tour, just completed a di

6、e stamping process. (2) composite model is only one station, in a press tour, at the same station at the same time to complete more than two or two die stamping process. (3) progressive die (also known as the modulus of continuity) in the feeding direction, rough, with two or more of the station, at

7、 the press of a visit, work in different places on the completion of two or two successive road over stamping die process. chong called cold stamping die die-wide. cold stamping die is used in cold stamping die mold industry, and accessories required for high-performance structural ceramic materials

8、, preparation methods, high-performance ceramic materials, molds and accessories from the zirconium oxide and yttrium aluminum powder increases, pr element composition, preparation is the solution of zirconia, yttria solution, praseodymium oxide solution, according to a certain percentage of alumina

9、 solution when mixed liquor, ammonium bicarbonate infusion, by co-precipitation synthesis of ceramic materials, molds and accessories needed for raw materials, reaction precipitate generated by the treatment, drying, calcining and accessories by high performance ceramic mold material superfine powde

10、r, and then after forming, sintering, finishing, they will have high-performance ceramic materials, molds and accessories. advantages of this invention is the invention made of cold stamping dies and parts and long service life, the process does not appear in the press and its parts and stamping die

11、 bond generated the phenomenon of stamping surface is smooth, no glitches, can replace traditional high-speed steel, tungsten steel. die with the main parts die stamping tools is the main process equipment, stamping rely on the relative movement under the mold completed. processing time because the

12、upper and lower mold between the constant division and, if continued operation of the fingers of workers to enter or remain in the mold closed, there will certainly pose a serious threat to their personal safety. (a) of the mold main parts, function and safety requirements 1. working parts is a dire

13、ct punch to blank forming the working parts, therefore, it is the key to mold parts. punch not only sophisticated and complex, it should meet the following requirements: (1) be of sufficient strength, can not be broken or destroyed during stamping. (2) should be appropriate to its material and heat

14、treatment requirements, to prevent too high hardness and brittle fracture. 2. positioning parts positioning part is to determine the location of the parts installed blank, there are pins (board), gauge pin (plate), lead is sold, guide plate, knife set from the side, side pressure etc. design should

15、be considered when positioning parts easy to operate and should not have had orientation, location to facilitate observation, preferably in the forward position, contouring to correct the pin location and positioning. 3. binder, unloading and discharging parts binder components are blank holder, bin

16、der board. blank holder pressure can drawing blank holder force, thereby preventing billets under the action of the tangential pressure arch formed folds. the role of pressure plate to prevent movement and bounce blank. top of the device, discharge boards role is to facilitate the pieces and clean u

17、p waste. them by the spring, rubber and equipment, putting on the air-cushion support, can move up and down, knocking out pieces of the design should have enough top output, movement to the limited spaces. stripper plate area should be minimized or closed position in the operating groove milling out

18、 empty-handed. exposure of the stripper plate should have protection around the plate, to prevent finger inserted into or foreign objects inside, exposed surface edges should be blunt down. 4. guide parts and guide sleeve guide pin is the most widely used part of a guide. its role is to ensure punch

19、 the punching clearance when accurate match. therefore, the guide posts, guide cover the gap should be less than the blanking clearance. guide post located next mold base, to ensure that the stroke bottom dead center, the lead column in the template on the face over the top for at least 5 to 10 mm.

20、guide columns should be arranged far away from the module and the pressure plate in the area, so the operators arms do not get to take over the lead column material. 5. supporting and clamping the upper and lower parts which includes templates, die handle, fixed plate punch, plate, stopper, etc. up

21、and down the template is the basis of the cold die parts, other parts are respectively fixed at the top. template plane size, especially around the direction to be compatible with the workpiece, too large or too small are not conducive to action. some molds (blanking, punching type mold) to the piec

22、es of convenience, be set up under the mold plate. at this time the best and the template plate connected between the screw, the two plate thickness should be absolutely equal. plate spacing out the pieces to be able to prevail, not too much, so as not to break the template. 6. fastening parts which

23、 includes screws, nuts, springs, pins, washers, etc., are generally used standard parts. die more with the amount of standard parts, design choice and flexibility should be tightened to ensure the top out of the need to avoid exposure to the surface fastener operating position, the staff and impede

24、operation to prevent bumps. die with the development of since reform and opening, with the rapid development of the national economy, the market demand with the growing die. in recent years, die with the industry has been around 15% growth rate of the rapid development of industrial enterprises with

25、 ownership die components also changed dramatically, in addition to the professional mold factory outside of state-owned, collective, joint ventures, wholly-owned and private has been a rapid development. as with the accelerating pace of international integration, the increasing competition in the m

26、arket, it has been increasingly recognized product quality, cost, and new product development capacities. the cold die manufacturing is the most basic elements of the chain, one of the cold die manufacturing technology to measure a countrys manufacturing sector has become an important symbol of the

27、level, and largely determine the viability of enterprises. die with enterprises to increase in recent years many technological advances for investment, technological progress will be seen as an important driving force for enterprise development. some domestic enterprises have popularized the two-dim

28、ensional mold cad, and gradually began to use ug, pro / engineer, i-deas, euclid-is and other international common software, individual manufacturers have also introduced moldflow, c-flow, dynaform, optris and magmasoft etc. cae software, and successfully applied in stamping die design. a car cover

29、mold as the representative of a large stamping die manufacturing technology has made great progress, dongfeng motor corporation mold factory, mold manufacturers such as faw mold center has been able to produce some car cover mold. in addition, many research institutions and universities to carry out

30、 technology research and development of mold. after years of effort, in the mold cad / cae / cam technology has made remarkable progress; in improving quality and reducing mold die design and manufacturing cycle, and so contributed. although china die with the industry over the past decade has made

31、remarkable development, but in many ways compared with the industrialized countries there is still a large gap. for example, the precision machining equipment, processing equipment in die with the relatively low proportion; cad / cae / cam technology penetration is not high; many advanced mold techn

32、ology not widely so, resulting in a considerable number of large, sophisticated, complex and long die life with dependence on imports. with the continuous progress of science and technology, modern industrial production of increasingly complex and diverse, product performance and quality is ever inc

33、reasing, thus the cold stamping technology put forward higher requirements. in order to adapt to the cold stamping technology industry needs, cold stamping technology itself also in innovation and development. cold stamping technology idea is to improve and expand as much as possible the advantages

34、of the cold stamping process, to overcome its shortcomings. in the cold stamping technology development, should note the following aspects: (1) cold stamping technology process parameters should be properly identified and die with the work of some of the shape and size, to improve the quality of sta

35、mping parts and shorten the new product production cycle should be in strengthening the metal forming the basis of theoretical studies, to metal forming theory to practice can produce a direction, and gradually establish a close connection with the actual production of the advanced process of calcul

36、ation. abroad have begun to use plastic finite element method, automobile parts forming process of the stress and strain analysis and computer simulation to predict the forming part of a process plan on the possibilities and potential problems. (2) to accelerate product replacement, mold design to o

37、vercome the shortcomings of a long cycle. should vigorously carry out computer-aided design and manufacture of molds (cad / cam) research. in my country, paying particular attention to strengthening the multi-position progressive die cad / cam technology. (3) to meet the needs of mass production, an

38、d reduce labor intensity. should strengthen cold stamping of mechanized and automated, so that the average, small pieces of high-speed presses in a multi-position progressive die production, production reached a high degree of automation to further improve stamping productivity. (4) expand the scope

39、 of application of cold stamping production. so cold pressing both suitable for mass production, but also for small batch production; both the general accuracy of product production, but also can produce precision parts. should pay attention to development such as fine blanking (especially thick mat

40、erial fine blanking), forming high-energy, soft mold forming, pressure and processing new superplastic forming process, but also promote the easy mode (soft mode and the low melting point alloy mold), universal hybrid model, the use of cnc punch press and other equipment. in addition, the performanc

41、e improvement of sheet metal stamping, mold new material, die development of new processing methods should be further strengthened. die with life and countermeasures die with the life of the workpiece by punching out the number of terms. many factors affect the life die. there are die structure desi

42、gn, manufacture molds used in the punch and die materials, die quality and surface hardening heat treatment, precision die manufacturing parts and cold stamping materials selection. in addition, there are die installation, adjustment, use and maintenance. 1. die design on life (1) layout design of l

43、ayout methods and take the boundary value a great impact on the die life, too small to take the boundary value, often causing rapid wear and convex mold, die bite wounds on the. starting from material savings, take the boundary value smaller the better, but take the edge is less than some value, the

44、 cut surface of the mold and the quality of life adversely. there will be left behind in the blanking die q-gap were to produce spare parts glitch, or even damage the die edge, reduce die life. therefore, consider increasing the material utilization of the same time, parts must yield, quality and li

45、fe expectancy to determine the layout methods and take the boundary. (2) die structure prone to stress concentration on the cracking of the die structure, composite structure can be used or mosaic structure, and prestressed structure to enhance the mold life. (3) the impact of clearance when the gap

46、 is too small, compressed extrusion of interest, increased friction, increased wear, the wear side of aggravated discharge and push pieces after blanking time, materials and convex, the friction between die will cause wear and tear than the end edge on the side of the grinding much, but also easily

47、lead to convex, concave mold temperature is high, the adsorption of metal debris in the side edge to form a metal tumor, so that male and female die chipping or expansion occurs crack phenomenon. therefore, the gap is too small to die life very bad. gap is too large will increase the punch and the d

48、ie face the edge of the concentration of stress, resulting in a sharp increase in stress, so blade edge quickly lose angular yield deformation. therefore, addition of blanking force, thereby enabling faster edge edge wear, reduce die life. but in order to reduce the male and female die wear, extendi

49、ng mold life, while ensuring quality of stamping pieces under the premise that larger space designed properly it is necessary. (4) die-oriented structure of the life of a reliable guide for the working parts reduce wear, prevent male and female die bite wound is very effective. in particular, non-sm

50、all-q gap q gap or die, compound die and multi-position progressive die even more important. to improve the die life, must be based on processes and the demand of precision, the correct choice-oriented form and orientation accuracy, the choice should be higher than the accuracy-oriented convex, conc

51、ave mold with precision. (5) the impact of cold stamping materials, cold stamping materials selected should meet the design requirements of workpieces and stamping process requirements, or easy to mold damage and reduce mold life. poor surface quality of cold stamping, punching, cracking when the wo

52、rkpiece is also easy to scratch mold. bad cold stamping plastic materials, deformation is small, easy to press when the workpiece rupture, but also easy to scratch mold. in addition, the material thickness tolerances shall comply with national standards. die because of a certain thickness of materia

53、l suitable for forming, bending, flanging, drawing die of the male and female die structure gap is directly determined by the thickness of the material. therefore, uneven thickness, will result in waste generation and mold damage. 2. die die life of die die life of a mold material properties, chemic

54、al composition, structure, hardness and comprehensive reflection of metallurgical quality. among them, the material properties and heat treatment affect the quality of the most obvious. mold material properties on the impact of die life is great. if the same workpiece, using a different mold materia

55、l of the bending test, the test results: the 9mn2v material, the life of 5 million; with crl2mov nitriding, the life of up to 40 million. therefore, the choice of materials, the batch size should be based on workpiece, rational use of mold materials. the hardness of the die parts to die life a great

56、 impact. but not the higher hardness, longer die life. this is because the hardness and strength, toughness and abrasion resistance are closely related. some die demands of high hardness, long life. such as the use of t10 steel dies, hardness 54 58hrc, only washed thousands of times a burr on the wo

57、rkpiece great. if the hardness to 60 64hrc, the grinding life of up to 2 to 3 million. however, if continue to improve hardness, fracture occurs earlier. some die hardness should not be too high, as the die manufacturing using crl2mov 58 62hrc hardness, the general life of 2-3 million, invalid form

58、of chipping and cracking, and if the hardness down to 54 58hrc, life expectancy increased to 5 60 000, but decreased to 50 53hrc hardness appears easy to blunt the die edge phenomenon. thus, mold hardness must be based on material properties and failure modes may be. should enable the hardness, stre

59、ngth, toughness and wear resistance, resistance to fatigue strength needed to achieve a particular stamping process the best match. 3. the surface of the mold heat treatment to strengthen the quality and impact on life mold heat treatment the nature and quality of life of the mold a great impact. practice shows that the die parts of the quenching distortion and cracking, early fracture during use, while the metallurgical and materials quality, forging quality, mold structure and process related, but related more